ASTM B241 Grade 6061 T6 Extruded Pipe – 25 mm & Larger
ASTM 6061 is a readily available alloy that has good surface finish and ability to be anodized.Easy of weldability and brazability with nice surface finish. Resistance to corrosion from seawater and atmospheric conditions. Suitable for hot forging.
Quantity: 1 PCSProperties
General
| Property | Value | Comment |
|---|---|---|
Density | 2.7 g/cm³ | Typical for Wrought 6000 Series Aluminium |
Mechanical
| Property | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|
Elastic modulus | 70.0 GPa | Typical for Wrought 6000 Series Aluminium | |||
Elongation | 9.0 % | T6 (Extruded); Pipe Size 25 and over | ASTM B241 | Pipe | |
10.0 % | T6 (Extruded); Pipe Size 25 and over | ASTM B241 | Pipe | A50 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 6000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] | Typical for Wrought 6000 Series Aluminium | |||
Shear modulus | 26.0 - 26.5 GPa | Typical for Wrought 6000 Series Aluminium | |||
Tensile strength | 260.0 MPa | T6 (Extruded); Pipe Size 25 and over | ASTM B241 | Pipe |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 1.6e-05 - 2.4e-05 1/K | Typical for Wrought 6000 Series Aluminium |
Melting point | 555.0 - 655.0 °C | Typical for Wrought 6000 Series Aluminium |
Specific heat capacity | 887.0 - 963.0 J/(kg·K) | Typical for Wrought 6000 Series Aluminium |
Thermal conductivity | 170.0 - 220.0 W/(m·K) | Typical for Wrought 6000 Series Aluminium |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 21000000.0 - 34000000.0 S/m | Typical for Wrought 6000 Series Aluminium |
Electrical resistivity | 2.9e-08 - 5e-08 Ω·m | Typical for Wrought 6000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chromium | 0.04 - 0.35 % | T6 (Extruded); Pipe Size 25 and over | ASTM B241 | Pipe |
Copper | 0.15 - 0.4 % | T6 (Extruded); Pipe Size 25 and over | ASTM B241 | Pipe |
Iron | 0.7 | T6 (Extruded); Pipe Size 25 and over | ASTM B241 | Pipe |
Magnesium | 0.8 - 1.2 % | T6 (Extruded); Pipe Size 25 and over | ASTM B241 | Pipe |
Manganese | 0.15 | T6 (Extruded); Pipe Size 25 and over | ASTM B241 | Pipe |
Silicon | 0.4 - 0.8 % | T6 (Extruded); Pipe Size 25 and over | ASTM B241 | Pipe |
Titanium | 0.15 | T6 (Extruded); Pipe Size 25 and over | ASTM B241 | Pipe |
Zinc | 0.25 | T6 (Extruded); Pipe Size 25 and over | ASTM B241 | Pipe |
Technological properties
| Property | ||
|---|---|---|
| Workability | Excellent workability. | |
Metal
- ASTM B241 Grade 6061‑T6 Aluminum Alloy – High Strength & Corrosion Resistance
- ASTM B211 Grade 6061 T89/T94 Aluminum Alloy – Properties & Applications
- ASTM B241 Grade 6061 T6 (Drawn) – High‑Performance Aluminium Pipe, 25mm and Under
- ASTM B241 Grade 6061‑T6 Extruded Pipe – High‑Performance Aluminium for Under 25 in.
- ASTM B241 Grade 6061-T1 Aluminium Alloy – High Performance & Corrosion Resistance
- ASTM B241 Grade 6061 T42 Aluminum Alloy – Superior Strength & Corrosion Resistance
- ASTM B241 Grade 6061-T5/6 Aluminium Alloy – Key Properties & Applications
- ASTM B241 Grade 6061‑T6 Drawn Pipe – Size 25 & Larger
- ASTM B241 Grade 6061 O Aluminum Alloy – Superior Strength & Corrosion Resistance
- ASTM B241 Grade 6061 T6 Extruded Pipe – 25 mm & Larger