EN 573-3 Grade 3.0285 H111 – Premium Aluminium Alloy for Engineering
Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.7 g/cm³ | H111 | EN 573-3, EN 485 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Bending angle 180° | 0.5 °/t | H111 | EN 573-3, EN 485 | |
Bending angle 90° | 0.5 °/t | H111 | EN 573-3, EN 485 | |
Elastic modulus | 70.0 GPa | H111 | EN 573-3, EN 485 | |
Hardness, Brinell | 18.0 [-] | H111 | EN 573-3, EN 485 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 1000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] | Typical for Wrought 1000 Series Aluminium | ||
Shear modulus | 25.9 GPa | Typical for Wrought 1000 Series Aluminium | ||
Tensile strength | 60.0 - 90.0 MPa | H111 | EN 573-3, EN 485 |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.35e-05 1/K | H111 | EN 573-3, EN 485 | |
100 °C | 2.35e-05 1/K | H111 | EN 573-3, EN 485 | ||
Melting point | 659.0 °C | H111 | EN 573-3, EN 485 | ||
Specific heat capacity | 900.0 - 963.0 J/(kg·K) | Typical for Wrought 1000 Series Aluminium | |||
Thermal conductivity | 225 W/(m·K) | H111 | EN 573-3, EN 485 |
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 34500000.0 - 35000000.0 S/m | H111 | EN 573-3, EN 485 |
Electrical resistivity | 2.86e-08 - 2.9e-08 Ω·m | H111 | EN 573-3, EN 485 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 99.8 % | H111 | EN 573-3, EN 485 |
Copper | 0.03 % | H111 | EN 573-3, EN 485 |
Gallium | 0.03 % | H111 | EN 573-3, EN 485 |
Iron | 0.15 % | H111 | EN 573-3, EN 485 |
Magnesium | 0.02 % | H111 | EN 573-3, EN 485 |
Manganese | 0.02 % | H111 | EN 573-3, EN 485 |
Silicon | 0.15 % | H111 | EN 573-3, EN 485 |
Titanium | 0.02 % | H111 | EN 573-3, EN 485 |
Zinc | 0.06 % | H111 | EN 573-3, EN 485 |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | decorative: very good, Protective: very good | |
| Brazing | hard brazing (with flux/ without flux): very good / very good, friction soldering: very good, soft brazing with flux: very good | |
| Workability | Bending / Spinning (cold): very good / very good, Impact extrusion (cold): very good, Deep drawing / upsetting (Condition) very good (H14) / very good (H12) | |
Metal
- EN 573-3 Grade 3.0915 (H111) – Premium Aluminium Alloy
- EN 573-3 Grade 3.3326 H111 – Detailed Mechanical Properties of 5000 Series Aluminium
- EN 573-3 Grade 3.0285 H112: Comprehensive Material Properties
- EN 573-3 Grade 3.0505 H111 Aluminium Alloy - Technical Specifications
- AW‑5186 H111 Aluminium Alloy – EN 573‑3 Certified for High‑Performance Applications
- EN 573-3 Grade 3.0257 H111 Aluminium Alloy Specifications
- EN 573-3 Grade 3.3549 H111 Aluminium Alloy – Technical Specifications and R&D Services
- EN 573-3 Grade 3.1325 H111 – Aluminium Alloy Properties & Standards
- EN 573-3 Grade 3.2315 H111 – Detailed Aluminium Alloy Specifications
- EN 573-3 Grade 3.0285 H26 – Comprehensive Technical Specifications