EN 573-3 Grade 3.0285 H26 – Comprehensive Technical Specifications
Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.7 g/cm³ | H26 | EN 573-3, EN 485 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Bending angle 90° | 0.5 °/t | H26 | EN 573-3, EN 485 | |
1.0 °/t | H26 | EN 573-3, EN 485 | ||
Elastic modulus | 70.0 GPa | H26 | EN 573-3, EN 485 | |
Hardness, Brinell | 35.0 [-] | H26 | EN 573-3, EN 485 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 1000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] | Typical for Wrought 1000 Series Aluminium | ||
Shear modulus | 25.9 GPa | Typical for Wrought 1000 Series Aluminium | ||
Tensile strength | 110.0 - 150.0 MPa | H26 | EN 573-3, EN 485 |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.35e-05 1/K | H26 | EN 573-3, EN 485 | |
100 °C | 2.35e-05 1/K | H26 | EN 573-3, EN 485 | ||
Melting point | 659.0 °C | H26 | EN 573-3, EN 485 | ||
Specific heat capacity | 900.0 - 963.0 J/(kg·K) | Typical for Wrought 1000 Series Aluminium | |||
Thermal conductivity | 225 W/(m·K) | H26 | EN 573-3, EN 485 |
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 34500000.0 - 35000000.0 S/m | H26 | EN 573-3, EN 485 |
Electrical resistivity | 2.86e-08 - 2.9e-08 Ω·m | H26 | EN 573-3, EN 485 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 99.8 % | H26 | EN 573-3, EN 485 |
Copper | 0.03 % | H26 | EN 573-3, EN 485 |
Gallium | 0.03 % | H26 | EN 573-3, EN 485 |
Iron | 0.15 % | H26 | EN 573-3, EN 485 |
Magnesium | 0.02 % | H26 | EN 573-3, EN 485 |
Manganese | 0.02 % | H26 | EN 573-3, EN 485 |
Silicon | 0.15 % | H26 | EN 573-3, EN 485 |
Titanium | 0.02 % | H26 | EN 573-3, EN 485 |
Zinc | 0.06 % | H26 | EN 573-3, EN 485 |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | decorative: very good, Protective: very good | |
| Brazing | hard brazing (with flux/ without flux): very good / very good, friction soldering: very good, soft brazing with flux: very good | |
| Workability | Bending / Spinning (cold): very good / very good, Impact extrusion (cold): very good, Deep drawing / upsetting (Condition) very good (H14) / very good (H12) | |
Metal
- EN 573-3 Grade 3.0915 H26 Aluminium Alloy – Key Properties & Standards
- EN 573-3 Grade 3.0505 H26 – Aluminum Alloy Properties & Standards
- AW‑1350 H26 Aluminum Alloy – EN 573‑3 Grade Specifications & Properties
- EN 573-3 Grade 3.0257 H26 – Premium Aluminum Alloy Properties
- EN 573-3 Grade 3.0285 H112: Comprehensive Material Properties
- EN 573-3 Grade 3.3315 (H26) – Standard Aluminum Alloy
- EN 573-3 Grade 3.3316 H26 Steel – Specifications & Mechanical Properties
- EN 573-3 Grade 3.0275 H26 – High-Strength Steel with R&D Support
- EN 573-3 Grade 3.0515 H26 – Premium Structural Steel
- EN 573-3 Grade 3.3555 H26 – Key Mechanical Properties & Standards