EN 573-3 Grade 3.3525 H26 – Comprehensive Material Specification
Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.68 g/cm³ | H26 | EN 573-3, EN 1592, EN 485, EN 754 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Bending angle 180° | 3.0 °/t | H26 | EN 573-3, EN 485 | |
Bending angle 90° | 1.0 °/t | H26 | EN 573-3, EN 485 | |
1.5 °/t | H26 | EN 573-3, EN 485 | ||
2.0 °/t | H26 | EN 573-3, EN 485 | ||
3.0 °/t | H26 | EN 573-3, EN 485 | ||
Elastic modulus | 70.0 GPa | H26 | EN 573-3, EN 1592, EN 485, EN 754 | |
Hardness, Brinell | 69.0 [-] | H26 | EN 573-3, EN 485 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Shear modulus | 26.3 GPa | H26 | EN 573-3, EN 1592, EN 485, EN 754 | |
Tensile strength | 220.0 - 260.0 MPa | H26 | EN 573-3, EN 754 | |
230.0 - 270.0 MPa | H26 | EN 573-3, EN 485 | ||
245.0 MPa | H26 | EN 573-3, EN 1592 |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.3699999999999997e-05 1/K | H26 | EN 573-3, EN 1592, EN 485, EN 754 | |
100 °C | 2.3699999999999997e-05 1/K | H26 | EN 573-3, EN 1592, EN 485, EN 754 | ||
Max service temperature | 150.0 °C | Typical for Wrought 5000 Series Aluminium | |||
Melting point | 610.0 - 650.0 °C | H26 | EN 573-3, EN 1592, EN 485, EN 754 | ||
Specific heat capacity | 879.0 - 963.0 J/(kg·K) | Typical for Wrought 5000 Series Aluminium | |||
Thermal conductivity | 140.0 - 160.0 W/(m·K) | H26 | EN 573-3, EN 1592, EN 485, EN 754 |
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 25000000.0 - 30000000.0 S/m | H26 | EN 573-3, EN 1592, EN 485, EN 754 |
Electrical resistivity | 3.33e-08 - 4e-08 Ω·m | H26 | EN 573-3, EN 1592, EN 485, EN 754 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Chromium | 0.15 % | H26 | EN 573-3, EN 1592, EN 485, EN 754 |
Copper | 0.15 % | H26 | EN 573-3, EN 1592, EN 485, EN 754 |
Iron | 0.50 % | H26 | EN 573-3, EN 1592, EN 485, EN 754 |
Magnesium | 1.7 - 2.4 % | H26 | EN 573-3, EN 1592, EN 485, EN 754 |
Manganese | 0.1 - 0.5 % | H26 | EN 573-3, EN 1592, EN 485, EN 754 |
Silicon | 0.4 % | H26 | EN 573-3, EN 1592, EN 485, EN 754 |
Titanium | 0.15 % | H26 | EN 573-3, EN 1592, EN 485, EN 754 |
Zinc | 0.15 % | H26 | EN 573-3, EN 1592, EN 485, EN 754 |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | decorative: sufficient, Protective: very good | |
| Brazing | hard brazing (with flux/ without flux): sufficient / poor, friction soldering: good, soft brazing with flux: sufficient | |
| Corrosion properties | Seawater: good, weathering: very good | |
| Workability | Bending / Spinning (cold): good / acceptable, Impact extrusion (cold): acceptable, Deep drawing / upsetting (Condition) good (O) / acceptable (H12) | |
Metal
- EN 573-3 Grade 3.0915 H26 Aluminium Alloy – Key Properties & Standards
- EN 573-3 Grade 3.0505 H26 – Aluminum Alloy Properties & Standards
- AW‑1350 H26 Aluminum Alloy – EN 573‑3 Grade Specifications & Properties
- EN 573-3 Grade 3.0257 H26 – Premium Aluminum Alloy Properties
- EN 573-3 Grade 3.3315 (H26) – Standard Aluminum Alloy
- EN 573-3 Grade 3.3316 H26 Steel – Specifications & Mechanical Properties
- EN 573-3 Grade 3.3525 H44 – High-Strength Aluminium with Superior Mechanical Properties
- EN 573-3 Grade 3.3525 H46 Aluminium Alloy – Key Properties & Standards
- EN 573-3 Grade 3.3525 H48 Aluminium – Properties & Standards
- EN 573-3 Grade 3.3525 H26 – Comprehensive Material Specification