AA 1060 H16 Aluminium Standard – Key Properties & Specifications
Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.705 g/cm³ | H16 | AA Standards, ASTM B209, ASTM B211 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Bending Fatigue Strength | 45.0 MPa | H16 | AA Standards | |
Elastic modulus | 69.0 GPa | H16 | AA Standards, ASTM B209, ASTM B211 | |
Hardness, Brinell | 30.0 [-] | H16 | AA Standards | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 1000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] | Typical for Wrought 1000 Series Aluminium | ||
Shear modulus | 25.9 GPa | Typical for Wrought 1000 Series Aluminium | ||
Tensile strength | 95.0 - 130.0 MPa | H16 | AA Standards, ASTM B209 | |
110.0 MPa | H16 | AA Standards, ASTM B211 | ||
115.0 MPa | H16 | AA Standards |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.36e-05 1/K | H16 | AA Standards, ASTM B209, ASTM B211 | |
100 °C | 2.36e-05 1/K | H16 | AA Standards, ASTM B209, ASTM B211 | ||
Melting point | 645.0 - 655.0 °C | H16 | AA Standards, ASTM B209, ASTM B211 | ||
Specific heat capacity | 900.0 - 963.0 J/(kg·K) | Typical for Wrought 1000 Series Aluminium | |||
Thermal conductivity | 230.0 - 234.0 W/(m·K) | H16 | AA Standards, ASTM B209, ASTM B211 |
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 35000000.0 - 36000000.0 S/m | H16 | AA Standards, ASTM B209, ASTM B211 |
Electrical resistivity | 2.78e-08 - 2.86e-08 Ω·m | H16 | AA Standards, ASTM B209, ASTM B211 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 99.6 % | H16 | AA Standards, ASTM B209, ASTM B211 |
Copper | 0.05 % | H16 | AA Standards, ASTM B209, ASTM B211 |
Iron | 0.35 % | H16 | AA Standards, ASTM B209, ASTM B211 |
Magnesium | 0.03 % | H16 | AA Standards, ASTM B209, ASTM B211 |
Manganese | 0.03 % | H16 | AA Standards, ASTM B209, ASTM B211 |
Silicon | 0.25 % | H16 | AA Standards, ASTM B209, ASTM B211 |
Titanium | 0.03 % | H16 | AA Standards, ASTM B209, ASTM B211 |
Vanadium | 0.05 % | H16 | AA Standards, ASTM B209, ASTM B211 |
Zinc | 0.05 % | H16 | AA Standards, ASTM B209, ASTM B211 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: possible with commercial processes and methods | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: not suitable (O, H12), poor (H14, H16, H18) | |
| Workability | general (condition): good (O, H12, H14), acceptable (H16, H18) | |
Metal
- AA 3005 H16 Aluminium Grade: Standards & Properties
- AA Standard Grade 1435 H16: Key Mechanical Properties & Specifications
- AA 1350 Grade H16 – Comprehensive Mechanical & Thermal Properties
- AA 1060 H26 Aluminium – ASTM B209 Standards and Properties
- AA Standards Grade 1060 H28 Aluminium Alloy – Properties & Specifications
- AA Standards Grade 3105 H16 – Key Mechanical & Physical Properties
- AA 1060 H22 Aluminium Alloy – Full Grade Specifications & Mechanical Properties
- AA Standards Grade 1060 H24 – Properties & Specifications
- AA Standards Grade 1060 O – Complete Material Specifications & Standards
- AA 5005 H16 – Durable, Corrosion‑Resistant Aluminum for Marine Applications