DIN 17172 Grade StE 320.7 TM: Thermomechanically Treated Steel for High-Pressure Pipelines
The steel StE 320.7 TM is produced as welded tube in the conditions thermomechanical treated. Tubes of this steel are conform acc. 5L, 5LX and 5LS of the American Petroleum Institute (API). The Attention should be paid to the technical regulation for combustible liquids TRbF 301. Application: pipelines for combustible liquids (e.g. petroleum and his products) and for compressed or liquid combustible gases
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 7.85 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | -100.0 °C | 217 GPa | |
20.0 °C | 212 GPa | ||
100.0 °C | 207 GPa | ||
200.0 °C | 199 GPa | ||
300.0 °C | 192 GPa | ||
400.0 °C | 184 GPa | ||
500.0 °C | 175 GPa | ||
600.0 °C | 164 GPa | ||
Elongation, transverse | 20.0 °C | 21 % | |
Poisson's ratio | 20.0 °C | 0.28 [-] | |
Shear modulus | 23.0 °C | 82 GPa | Typical for Low Carbon Steel |
Tensile strength | 20.0 °C | 460 - 580 MPa | |
Tensile strength, transverse | 20.0 °C | 460 - 580 MPa | |
Yield strength | 20.0 °C | 320 MPa | |
Yield strength, transverse | 20.0 °C | 320 MPa | |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | -100.0 °C | 1.08E-5 1/K | |
20.0 °C | 1.19E-5 1/K | ||
100.0 °C | 1.25E-5 1/K | ||
200.0 °C | 1.3E-5 1/K | ||
300.0 °C | 1.36E-5 1/K | ||
400.0 °C | 1.41E-5 1/K | ||
500.0 °C | 1.45E-5 1/K | ||
600.0 °C | 1.49E-5 1/K | ||
Max service temperature | 500 °C | Typical for Carbon Steel | |
Melting point | 1480 - 1526 °C | Typical for Low Carbon Steel | |
Specific heat capacity | -100.0 °C | 423 J/(kg·K) | |
20.0 °C | 461 J/(kg·K) | ||
100.0 °C | 479 J/(kg·K) | ||
200.0 °C | 499 J/(kg·K) | ||
300.0 °C | 517 J/(kg·K) | ||
400.0 °C | 536 J/(kg·K) | ||
500.0 °C | 558 J/(kg·K) | ||
600.0 °C | 587 J/(kg·K) | ||
Thermal conductivity | 20.0 °C | 56.9 W/(m·K) | |
100.0 °C | 56.4 W/(m·K) | ||
200.0 °C | 53.5 W/(m·K) | ||
300.0 °C | 49.4 W/(m·K) | ||
400.0 °C | 45.2 W/(m·K) | ||
500.0 °C | 41.3 W/(m·K) | ||
600.0 °C | 37.6 W/(m·K) | ||
Thermal diffusivity | 20.0 °C | 15.7 mm²/s | |
100.0 °C | 14.5 mm²/s | ||
200.0 °C | 12.9 mm²/s | ||
300.0 °C | 11.2 mm²/s | ||
400.0 °C | 9.6 mm²/s | ||
500.0 °C | 7.9 mm²/s | ||
600.0 °C | 6.3 mm²/s | ||
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical resistivity | 20.0 °C | 1.83E-7 Ω·m |
100.0 °C | 2.27E-7 Ω·m | |
200.0 °C | 2.95E-7 Ω·m | |
300.0 °C | 3.8E-7 Ω·m | |
400.0 °C | 4.81E-7 Ω·m | |
500.0 °C | 5.99E-7 Ω·m | |
600.0 °C | 7.38E-7 Ω·m | |
Magnetic
| Property | Value | Comment |
|---|---|---|
Curie temperature | 770 °C | Typical for Low Carbon Steel |
Chemical properties
| Property | Value |
|---|---|
Carbon | 0.12 % |
Manganese | 0.7 - 1.5 % |
Phosphorus | 0.04 % |
Silicon | 0.4 % |
Sulfur | 0.025 % |
Metal
- DIN 17440 Grade X4CrNi18-12 Heat‑Treated Stainless Steel – Corrosion‑Resistant Wire & Components
- DIN 17440 Grade X6Cr17 Heat Treated – Premium Corrosion‑Resistant Stainless Steel
- DIN 1681 GS-60 Heat‑Treated Steel – Superior Wear Resistance & Strength
- DIN 17172 Grade StE 210.7 Hot‑Finished Steel Tubes for Petroleum and Gas Pipelines
- DIN 17172 Grade StE 240.7 – Hot Finished Steel Tubes for Combustible Liquids
- DIN 17172 Grade StE 290.7 – Hot Finished Steel Tubes for Combustible Liquids
- DIN 17172 Grade StE 290.7 TM – Thermomechanically Treated Steel Tubes for Robust Combustible Liquid Pipelines
- DIN 17172 Grade StE 320.7 Hot-Finished Tubes – Seamless & Welded, API 5L/5LX/5LS Certified
- DIN 17172 Grade StE 360.7 – Hot Finished Seamless or Welded Tubes for Combustible Liquid Pipelines
- DIN 17172 Grade StE 360.7 TM – Thermomechanically Treated Steel for API 5L Pipelines