DIN 1681 GS-60 Heat‑Treated Steel – Superior Wear Resistance & Strength
GS-52 for castings without special stress with good wearing properties, like coatings, bearing rollers, beater heads, hammers. For castings with static or dynamic stress for cog wheels, impellers, sprocket wheels, cranks, baffle plates. Suitable for surface hardening. Application between -10 and +300 °C.
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 7.85 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 20.0 °C | 196 GPa | |
Elongation | 20.0 °C | 15 % | |
Poisson's ratio | 23.0 °C | 0.29 [-] | Typical for Low Carbon Steel |
Reduction of area | 20.0 °C | 21 % | |
Shear modulus | 23.0 °C | 82 GPa | Typical for Low Carbon Steel |
Tensile strength | 20.0 °C | 600 MPa | |
Yield strength | 20.0 °C | 300 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.32E-5 - 1.38E-5 1/K | Typical for Low Carbon Steel |
Max service temperature | 500 °C | Typical for Carbon Steel | |
Max service temperature, long | -10 - 300 °C | ||
Melting point | 1480 - 1526 °C | Typical for Low Carbon Steel | |
Specific heat capacity | 20.0 °C | 460 J/(kg·K) | |
Thermal conductivity | 20.0 °C | 50 W/(m·K) |
Electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Electrical resistivity | 23.0 °C | 1.43E-7 - 1.74E-7 Ω·m | Typical for Carbon Steel |
Magnetic
| Property | Value | Comment |
|---|---|---|
Curie temperature | 770 °C | Typical for Low Carbon Steel |
Metal
- ASTM A565 Grade 616 Heat-Treated Martensitic Stainless Steel: Key Properties & Performance
- DIN 17440 Grade X3CrTi17: Heat-Treated, Corrosion-Resistant Steel for Pressure Vessels
- DIN 17440 Grade X4CrNi18-12 Heat‑Treated Stainless Steel – Corrosion‑Resistant Wire & Components
- DIN 17440 Grade X6Cr17 Heat Treated – Premium Corrosion‑Resistant Stainless Steel
- High-Performance ZnAl27Cu2 Alloy – Grade G, Heat Treated for 120 °C Applications
- DIN EN 10283 Grade 1.4588: High‑Performance Austenitic Stainless Steel, Solution Heat Treated
- DIN 1681 GS-52 Heat-Treated Steel - Premium Wear Resistance for Heavy Machinery
- DIN 1681 GS-38 Heat-Treated Steel: Applications & Performance
- DIN 1681 GS‑45 Heat‑Treated Steel: Superior Strength for Heavy‑Duty Applications
- DIN 17172 Grade StE 290.7 TM – Thermomechanically Treated Steel Tubes for Robust Combustible Liquid Pipelines