EN 10217‑2 Grade St 42.8 Tube Steel – High‑Temperature Normalized Formed for Vessels & Petrochemical Use

High temperature tube steel for welded tubes and tube products. Applicable up to 500 °C wall temperature for continuous operation. Application: vessel construction, apparatus construction, petrochemical industry

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.85 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

212 GPa

100.0 °C

201 - 207 GPa

200.0 °C

199 - 200 GPa

300.0 °C

192 GPa

400.0 °C

183 - 184 GPa

500.0 °C

175 GPa

600.0 °C

164 - 166 GPa

Elongation

20.0 °C

21 %

Elongation, transverse

20.0 °C

19 %

Poisson's ratio

20.0 °C

0.28 [-]

Shear modulus

23.0 °C

82 GPa

Typical for Low Carbon Steel

Tensile strength

20.0 °C

410 - 530 MPa

Yield strength Rp0.2

20.0 °C

255 MPa

200.0 °C

205 MPa

250.0 °C

185 MPa

300.0 °C

160 MPa

350.0 °C

140 MPa

400.0 °C

130 MPa

450.0 °C

125 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.08E-5 1/K

20.0 °C

1.19E-5 1/K

100.0 °C

1.22E-5 - 1.25E-5 1/K

200.0 °C

1.29E-5 - 1.3E-5 1/K

300.0 °C

1.34E-5 - 1.36E-5 1/K

400.0 °C

1.4E-5 - 1.41E-5 1/K

500.0 °C

1.43E-5 - 1.45E-5 1/K

600.0 °C

1.46E-5 - 1.49E-5 1/K

Max service temperature

500 °C

Typical for Carbon Steel

Max service temperature, long

0 - 500 °C

Melting point

1480 - 1526 °C

Typical for Low Carbon Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 - 500 J/(kg·K)

200.0 °C

499 - 540 J/(kg·K)

300.0 °C

517 - 580 J/(kg·K)

400.0 °C

536 - 620 J/(kg·K)

500.0 °C

558 - 690 J/(kg·K)

600.0 °C

587 - 780 J/(kg·K)

Thermal conductivity

20.0 °C

53.4 W/(m·K)

100.0 °C

52.9 - 54 W/(m·K)

200.0 °C

50 - 50.3 W/(m·K)

300.0 °C

46.7 - 47 W/(m·K)

400.0 °C

43 - 43.3 W/(m·K)

500.0 °C

39.8 - 40 W/(m·K)

600.0 °C

36 - 36.7 W/(m·K)

Thermal diffusivity

20.0 °C

14.8 mm²/s

100.0 °C

13.6 mm²/s

200.0 °C

12.1 mm²/s

300.0 °C

10.6 mm²/s

400.0 °C

9.2 mm²/s

500.0 °C

7.7 mm²/s

600.0 °C

6.2 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

1.95E-7 Ω·m

100.0 °C

2.4E-7 - 2.42E-7 Ω·m

200.0 °C

3.1E-7 - 3.14E-7 Ω·m

300.0 °C

4E-7 - 4.02E-7 Ω·m

400.0 °C

5E-7 - 5.02E-7 Ω·m

500.0 °C

6.2E-7 - 6.21E-7 Ω·m

600.0 °C

7.55E-7 - 7.6E-7 Ω·m

Magnetic

PropertyValueComment

Curie temperature

770 °C

Typical for Low Carbon Steel

Chemical properties

PropertyValue

Carbon

0.21 %

Manganese

0.4 - 1.2 %

Phosphorus

0.04 %

Silicon

0.1 - 0.35 %

Sulfur

0.04 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. EN 10225 S355G7 Steel – Normalized or Normalized Formed (N) for Superior Workability and Weldability
    2. EN 10225 S355G8 Steel – Normalized or Normalized-Formed (+N) Grade
    3. DIN 2394-2: Grade St 28 Steel – Normalized & Normalized Formed (+N) Properties
    4. EN 10273 Grade P460NH – High-Temperature Normalized Steel for Pressure Vessel Applications
    5. EN 10217-2 Grade 16Mo3 Normalized Steel Tubes – Ideal for High-Temperature, High-Pressure Applications
    6. EN 10216-2 Grade St 45.8: High‑Temperature Normalized Tube Steel (+N) for Seamless Tubes
    7. EN 10217-2 Grade St 37.8: High‑Temperature Normalized Tube Steel for Industrial Use
    8. EN 10217-2 – P195GH Grade Stainless Steel Tubes (Normalized/Normalized Formed +N)
    9. EN 10217-2 Grade P235GH: Normalized or Normalized Formed (N) Steel Tubes for High-Temperature Applications
    10. EN 10217-2: Grade P265GH Normalized or Normalized‑Formed Steel for High‑Temperature Applications