AA 1100 H113: Premium 99% Aluminum Alloy for Superior Corrosion Resistance

AA 1100 is a soft, non-heat-treatable and low strength alloy that offers strong corrosion resistance. Composed of 99% aluminum and 0.12% copper, AA 1100 is purest grade of aluminum alloy available commercially.

Properties

General

Property	Value	Condition	Related Standards
Density	2.71 g/cm³	H113	AA Standards, ASTM B210, ASTM B483

Mechanical

Property	Value	Condition	Related Standards	Comment
Elastic modulus	69.0 GPa	H113	AA Standards, ASTM B210, ASTM B483
Plane-Strain Fracture Toughnes	22.0 - 35.0 MPa·√m			Typical for Wrought 1000 Series Aluminium
Poisson's ratio	0.33 [-]			Typical for Wrought 1000 Series Aluminium
Shear modulus	25.9 GPa			Typical for Wrought 1000 Series Aluminium
Tensile strength	75.0 MPa	H113	AA Standards, ASTM B210, ASTM B483

Thermal

Property	Temperature	Value	Condition	Related Standards	Comment
Coefficient of thermal expansion	20 °C	2.36e-05 1/K	H113	AA Standards, ASTM B210, ASTM B483
	100 °C	2.36e-05 1/K	H113	AA Standards, ASTM B210, ASTM B483
Melting point		640.0 - 655.0 °C	H113	AA Standards, ASTM B210, ASTM B483
Specific heat capacity		900.0 - 963.0 J/(kg·K)			Typical for Wrought 1000 Series Aluminium
Thermal conductivity		218.0 - 222.0 W/(m·K)	H113	AA Standards, ASTM B210, ASTM B483

Electrical

Property	Value	Condition	Related Standards
Electrical conductivity	33000000.0 - 34000000.0 S/m	H113	AA Standards, ASTM B210, ASTM B483
Electrical resistivity	2.94e-08 - 3.03e-08 Ω·m	H113	AA Standards, ASTM B210, ASTM B483

Chemical properties

Property	Value	Condition	Related Standards
Aluminium	99.0 %	H113	AA Standards, ASTM B210, ASTM B483
Copper	0.05 - 0.2 %	H113	AA Standards, ASTM B210, ASTM B483
Manganese	0.05 %	H113	AA Standards, ASTM B210, ASTM B483
Zinc	0.1 %	H113	AA Standards, ASTM B210, ASTM B483

Technological properties

Property
Brazing	general: possible with commercial processes and methods
Corrosion properties	Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere
General machinability	General: not suitable (O, H12), poor (H14, H16, H18)
Workability	general (condition): good (O, H12, H14), acceptable (H16), poor(H18)

AA Standards Grade 1060 O – Complete Material Specifications & Standards AA1100 H28 Aluminum Alloy: Premium Corrosion-Resistant Grade

Metal