AA 1100 H112: Premium Corrosion-Resistant Aluminum Alloy
AA 1100 is a soft, non-heat-treatable and low strength alloy that offers strong corrosion resistance. Composed of 99% aluminum and 0.12% copper, AA 1100 is purest grade of aluminum alloy available commercially.
Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.71 g/cm³ | H112 | AA Standards, ASTM B209, ASTM B211, ASTM B241, ASTM B247 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Elastic modulus | 69.0 GPa | H112 | AA Standards, ASTM B209, ASTM B211, ASTM B241, ASTM B247 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 1000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] | Typical for Wrought 1000 Series Aluminium | ||
Shear modulus | 25.9 GPa | Typical for Wrought 1000 Series Aluminium | ||
Tensile strength | 75.0 MPa | H112 | AA Standards, ASTM B211, ASTM B241, ASTM B247 | |
80.0 MPa | H112 | AA Standards, ASTM B209 | ||
85.0 MPa | H112 | AA Standards, ASTM B209 | ||
90.0 MPa | H112 | AA Standards, ASTM B209 |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.36e-05 1/K | H112 | AA Standards, ASTM B209, ASTM B211, ASTM B241, ASTM B247 | |
100 °C | 2.36e-05 1/K | H112 | AA Standards, ASTM B209, ASTM B211, ASTM B241, ASTM B247 | ||
Melting point | 640.0 - 655.0 °C | H112 | AA Standards, ASTM B209, ASTM B211, ASTM B241, ASTM B247 | ||
Specific heat capacity | 900.0 - 963.0 J/(kg·K) | Typical for Wrought 1000 Series Aluminium | |||
Thermal conductivity | 218.0 - 222.0 W/(m·K) | H112 | AA Standards, ASTM B209, ASTM B211, ASTM B241, ASTM B247 |
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 33000000.0 - 34000000.0 S/m | H112 | AA Standards, ASTM B209, ASTM B211, ASTM B241, ASTM B247 |
Electrical resistivity | 2.94e-08 - 3.03e-08 Ω·m | H112 | AA Standards, ASTM B209, ASTM B211, ASTM B241, ASTM B247 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 99.0 % | H112 | AA Standards, ASTM B209, ASTM B211, ASTM B241, ASTM B247 |
Copper | 0.05 - 0.2 % | H112 | AA Standards, ASTM B209, ASTM B211, ASTM B241, ASTM B247 |
Manganese | 0.05 % | H112 | AA Standards, ASTM B209, ASTM B211, ASTM B241, ASTM B247 |
Zinc | 0.1 % | H112 | AA Standards, ASTM B209, ASTM B211, ASTM B241, ASTM B247 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: possible with commercial processes and methods | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: not suitable (O, H12), poor (H14, H16, H18) | |
| Workability | general (condition): good (O, H12, H14), acceptable (H16), poor(H18) | |
Metal
- AA Grade 1060 H112 Aluminium Standard – Key Properties & ASTM Specifications
- ASTM B241 Grade 1100 H112 Aluminum Alloy – Superior Corrosion Resistance & Purity
- AA 5154 H112 Aluminium Standard – Comprehensive Property Overview
- AA 3003 Aluminum Alloy: Grade 3003 H112 – High Corrosion Resistance & Excellent Weldability
- AA 5086 H112: High-Strength, Corrosion-Resistant Structural Aluminum Alloy
- AA 1100 H16 Aluminum Alloy – Pure, Corrosion‑Resistant & Ideal for Non‑Heat‑Treatable Applications
- AA 1100 H14 Aluminum Alloy – 99% Pure, Non-Heat-Treatable with Superior Corrosion Resistance
- AA 1100 H12 Aluminum: Premium Grade with Superior Corrosion Resistance
- AA 1100 H18 Aluminum Alloy – Premium Grade 1100 with Superior Corrosion Resistance
- AA 1100O Aluminum Alloy – Purest Grade with Superior Corrosion Resistance