AA Grade 1060 H112 Aluminium Standard – Key Properties & ASTM Specifications
Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.705 g/cm³ | H112 | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B345 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Elastic modulus | 69.0 GPa | H112 | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B345 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 1000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] | Typical for Wrought 1000 Series Aluminium | ||
Shear modulus | 25.9 GPa | Typical for Wrought 1000 Series Aluminium | ||
Tensile strength | 60.0 MPa | H112 | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B345 | |
70.0 MPa | H112 | AA Standards, ASTM B209 | ||
75.0 MPa | H112 | AA Standards, ASTM B209 |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.36e-05 1/K | H112 | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B345 | |
100 °C | 2.36e-05 1/K | H112 | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B345 | ||
Melting point | 645.0 - 655.0 °C | H112 | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B345 | ||
Specific heat capacity | 900.0 - 963.0 J/(kg·K) | Typical for Wrought 1000 Series Aluminium | |||
Thermal conductivity | 230.0 - 234.0 W/(m·K) | H112 | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B345 |
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 35000000.0 - 36000000.0 S/m | H112 | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B345 |
Electrical resistivity | 2.78e-08 - 2.86e-08 Ω·m | H112 | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B345 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 99.6 % | H112 | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B345 |
Copper | 0.05 % | H112 | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B345 |
Iron | 0.35 % | H112 | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B345 |
Magnesium | 0.03 % | H112 | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B345 |
Manganese | 0.03 % | H112 | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B345 |
Silicon | 0.25 % | H112 | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B345 |
Titanium | 0.03 % | H112 | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B345 |
Vanadium | 0.05 % | H112 | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B345 |
Zinc | 0.05 % | H112 | AA Standards, ASTM B209, ASTM B221, ASTM B241, ASTM B345 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: possible with commercial processes and methods | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: not suitable (O, H12), poor (H14, H16, H18) | |
| Workability | general (condition): good (O, H12, H14), acceptable (H16, H18) | |
Metal
- Grade 1060 H112 Aluminium – ASTM B241 Standard Tube Properties
- AA Standards Grade 1060 H113 Aluminium Alloy – Key Properties & Standards
- AA Standards Grade 1060 H18: Comprehensive Material Properties & Specifications
- AA Standards Grade 1060 O – Complete Material Specifications & Standards
- AA Standards 1060 H12 Aluminum: Properties, Standards & Specs
- AA 1060 H14 Aluminium Grade: Key Standards, Mechanical Properties & Density
- AA 5154 H112 Aluminium Standard – Comprehensive Property Overview
- AA 3003 Aluminum Alloy: Grade 3003 H112 – High Corrosion Resistance & Excellent Weldability
- AA 1100 H112: Premium Corrosion-Resistant Aluminum Alloy
- AA 5086 H112: High-Strength, Corrosion-Resistant Structural Aluminum Alloy