AA 1060 H14 Aluminium Grade: Key Standards, Mechanical Properties & Density
Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.705 g/cm³ | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B483 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Bending Fatigue Strength | 35.0 MPa | H14 | AA Standards | |
Elastic modulus | 69.0 GPa | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B483 | |
Hardness, Brinell | 26.0 [-] | H14 | AA Standards | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 1000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] | Typical for Wrought 1000 Series Aluminium | ||
Shear modulus | 25.9 GPa | Typical for Wrought 1000 Series Aluminium | ||
Tensile strength | 85.0 - 120.0 MPa | H14 | AA Standards, ASTM B209 | |
85.0 MPa | H14 | AA Standards, ASTM B210, ASTM B211, ASTM B234, ASTM B483 | ||
100.0 MPa | H14 | AA Standards |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.36e-05 1/K | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B483 | |
100 °C | 2.36e-05 1/K | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B483 | ||
Melting point | 645.0 - 655.0 °C | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B483 | ||
Specific heat capacity | 900.0 - 963.0 J/(kg·K) | Typical for Wrought 1000 Series Aluminium | |||
Thermal conductivity | 230.0 - 234.0 W/(m·K) | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B483 |
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 35000000.0 - 36000000.0 S/m | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B483 |
Electrical resistivity | 2.78e-08 - 2.86e-08 Ω·m | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B483 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 99.6 % | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B483 |
Copper | 0.05 % | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B483 |
Iron | 0.35 % | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B483 |
Magnesium | 0.03 % | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B483 |
Manganese | 0.03 % | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B483 |
Silicon | 0.25 % | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B483 |
Titanium | 0.03 % | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B483 |
Vanadium | 0.05 % | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B483 |
Zinc | 0.05 % | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B483 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: possible with commercial processes and methods | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: not suitable (O, H12), poor (H14, H16, H18) | |
| Workability | general (condition): good (O, H12, H14), acceptable (H16, H18) | |
Metal
- AA Standards Grade 1435 H14 – Detailed Mechanical Properties & Specifications
- ASTM B483 Grade 1060 H14 Aluminum – Detailed Properties & Specifications
- ASTM B210 Grade 1060 H14 Aluminum – Comprehensive Property Overview
- AA Standards Grade 1060 H113 Aluminium Alloy – Key Properties & Standards
- AA Grade 1060 H112 Aluminium Standard – Key Properties & ASTM Specifications
- AA Standards Grade 1060 H18: Comprehensive Material Properties & Specifications
- AA Standards Grade 1060 O – Complete Material Specifications & Standards
- AA Standards 1060 H12 Aluminum: Properties, Standards & Specs
- AA 3003 H14 Aluminum Alloy – High Corrosion Resistance & Superior Machinability
- AA 1100 H14 Aluminum Alloy – 99% Pure, Non-Heat-Treatable with Superior Corrosion Resistance