EN 573-3 Grade 3.0255 H16 – Premium Aludium Alloy for Advanced Applications

Quantity: One truck load – Specialty products on request.Additional services: Via Cindal (the Aludium R&D department): R&D services, benchmarking, chemical audits, material specification, process optimisation, quality monitoring, sample analysis, prototyping, training

Properties

General

Property	Value	Condition	Related Standards
Density	2.7 g/cm³	H16	EN 573-3, EN 1301, EN 485, EN 683, EN 754

Mechanical

Property	Value	Condition	Related Standards	Comment
Bending angle 90°	0.5 °/t	H16	EN 573-3, EN 485
	1.0 °/t	H16	EN 573-3, EN 485
	1.5 °/t	H16	EN 573-3, EN 485
Elastic modulus	69.0 GPa	H16	EN 573-3, EN 1301, EN 485, EN 683, EN 754
Elongation	1.0 %	H16	EN 573-3, EN 485, EN 683	A50
	2.0 %	H16	EN 573-3, EN 485	A50
	3.0 %	H16	EN 573-3, EN 1301
	3.0 %	H16	EN 573-3, EN 485, EN 754	A50
	4.0 %	H16	EN 573-3, EN 754	A100
Hardness, Brinell	39.0 [-]	H16	EN 573-3, EN 485
Plane-Strain Fracture Toughnes	22.0 - 35.0 MPa·√m			Typical for Wrought 1000 Series Aluminium
Poisson's ratio	0.33 [-]			Typical for Wrought 1000 Series Aluminium
Shear modulus	25.9 GPa	H16	EN 573-3, EN 1301, EN 485, EN 683, EN 754
Tensile strength	120.0 MPa	H16	EN 573-3, EN 1301
	120.0 - 160.0 MPa	H16	EN 573-3, EN 485, EN 683, EN 754

Thermal

Property	Temperature	Value	Condition	Related Standards
Coefficient of thermal expansion	-50 °C	2.17e-05 1/K	H16	EN 573-3, EN 1301, EN 485, EN 683, EN 754
	20 °C	2.17e-05 1/K	H16	EN 573-3, EN 1301, EN 485, EN 683, EN 754
	20 °C	2.35e-05 1/K	H16	EN 573-3, EN 1301, EN 485, EN 683, EN 754
	20 °C	2.4399999999999997e-05 1/K	H16	EN 573-3, EN 1301, EN 485, EN 683, EN 754
	20 °C	2.5399999999999997e-05 1/K	H16	EN 573-3, EN 1301, EN 485, EN 683, EN 754
	100 °C	2.35e-05 1/K	H16	EN 573-3, EN 1301, EN 485, EN 683, EN 754
	200 °C	2.4399999999999997e-05 1/K	H16	EN 573-3, EN 1301, EN 485, EN 683, EN 754
	300 °C	2.5399999999999997e-05 1/K	H16	EN 573-3, EN 1301, EN 485, EN 683, EN 754
Melting point		646.0 - 657.0 °C	H16	EN 573-3, EN 1301, EN 485, EN 683, EN 754
Specific heat capacity		900.0 J/(kg·K)	H16	EN 573-3, EN 1301, EN 485, EN 683, EN 754
Thermal conductivity		210.0 - 220.0 W/(m·K)	H16	EN 573-3, EN 1301, EN 485, EN 683, EN 754

Electrical

Property	Value	Condition	Related Standards
Electrical conductivity	34000000.0 - 36000000.0 S/m	H16	EN 573-3, EN 1301, EN 485, EN 683, EN 754
Electrical resistivity	2.78e-08 - 2.94e-08 Ω·m	H16	EN 573-3, EN 1301, EN 485, EN 683, EN 754

Chemical properties

Property	Value	Condition	Related Standards
Aluminium	99.5 %	H16	EN 573-3, EN 1301, EN 485, EN 683, EN 754
Copper	0.05 %	H16	EN 573-3, EN 1301, EN 485, EN 683, EN 754
Iron	0.40 %	H16	EN 573-3, EN 1301, EN 485, EN 683, EN 754
Magnesium	0.05 %	H16	EN 573-3, EN 1301, EN 485, EN 683, EN 754
Manganese	0.05 %	H16	EN 573-3, EN 1301, EN 485, EN 683, EN 754
Silicon	0.25 %	H16	EN 573-3, EN 1301, EN 485, EN 683, EN 754
Titanium	0.05 %	H16	EN 573-3, EN 1301, EN 485, EN 683, EN 754
Zinc	0.07 %	H16	EN 573-3, EN 1301, EN 485, EN 683, EN 754

Technological properties

Property
Anodizing	decorative: gut (EQ: sehr gut), Protective: very good
Brazing	hard brazing (with flux/ without flux): very good / very good, friction soldering: very good, soft brazing with flux: very good
Corrosion properties	Seawater: acceptable, weathering: good
Workability	Bending / Spinning (cold): very good / very good, Impact extrusion (cold): very good, Deep drawing / upsetting (Condition) very good (H14) / very good (H12)