DIN 1725‑1 Grade 3.3317 F: High‑Gloss Al99.85Mg1 Alloy for Superior Finish
The alloy Al99,85Mg1 belongs to the standardised glossing materials. It can be polished after preceding mechanical polishing chemically or electrolytically to high gloss. For using the high gloss surface a afterwards anodising is necessary. The degree of arranged reflection (gloss degree) dependents from the degree of purity of the alloy and the thickness of the produced anodising layer. The alloy Al99,85Mg1 is nature hard, i.e. with their a strength increase can be achieved only by cold forming. The material is well cold and warm fomrable, has a very good corrosion resistance and is also well anodically to be oxidized. Application: For metal goods, like building fittings, table-ware, flow pressed parts, autotrim and divides and for decoration and jeweller goods.
Properties
General
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Density | 2.69 g/cm³ | F | EN 573-3, EN 570 | ||
20.0 °C | 2.69 g/cm³ | F | DIN 1725-1, EN 573-3, EN 573-4 | Profile, Tube |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Elastic modulus | 20.0 °C | 70.0 | F | DIN 1725-1, EN 573-3, EN 573-4 | Profile, Tube | |
Elongation | 20.0 °C | 13.0 % | F | DIN 1725-1, EN 573-3, EN 573-4 | Profile | A10 |
20.0 °C | 15.0 % | F | DIN 1725-1, EN 573-3, EN 573-4 | Profile | ||
20.0 °C | 18.0 % | F | DIN 1725-1, EN 573-3, EN 573-4 | Tube | A10 | |
20.0 °C | 20.0 % | F | DIN 1725-1, EN 573-3, EN 573-4 | Tube | ||
Hardness, Brinell | 33.0 [-] | F | EN 573-3, EN 570 | |||
20.0 °C | 30.0 [-] | F | DIN 1725-1, EN 573-3, EN 573-4 | Profile, Tube | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||||
Poisson's ratio | 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||||
Shear modulus | 20.0 °C | 26.0 | F | DIN 1725-1, EN 573-3, EN 573-4 | Profile, Tube | |
Tensile strength | 20.0 °C | 100.0 MPa | F | DIN 1725-1, EN 573-3, EN 573-4 | Profile, Tube |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 2.2e-05 - 2.5e-05 1/K | Typical for Wrought 5000 Series Aluminium |
Max service temperature | 150.0 °C | Typical for Wrought 5000 Series Aluminium |
Melting point | 560.0 - 655.0 °C | Typical for Wrought 5000 Series Aluminium |
Specific heat capacity | 879.0 - 963.0 J/(kg·K) | Typical for Wrought 5000 Series Aluminium |
Thermal conductivity | 112.0 - 205.0 W/(m·K) | Typical for Wrought 5000 Series Aluminium |
Electrical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Electrical conductivity | 20.0 °C | 33000000.0 | F | DIN 1725-1, EN 573-3, EN 573-4 | Profile, Tube | |
Electrical resistivity | 3.3e-08 - 5e-08 Ω·m | Typical for Wrought 5000 Series Aluminium |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Iron | 0.08 % | F | DIN 1725-1, EN 573-3, EN 573-4 | Profile, Tube |
0.08 % | F | EN 573-3, EN 570 | ||
Magnesium | 0.7 - 1.1 % | F | DIN 1725-1, EN 573-3, EN 573-4, EN 570 | Profile, Tube |
Manganese | 0.03 % | F | DIN 1725-1, EN 573-3, EN 573-4, EN 570 | Profile, Tube |
Silicon | 0.08 % | F | DIN 1725-1, EN 573-3, EN 573-4, EN 570 | Profile, Tube |
Titanium | 0.02 % | F | DIN 1725-1, EN 573-3, EN 573-4, EN 570 | Profile, Tube |
Zinc | 0.05 % | F | DIN 1725-1, EN 573-3, EN 573-4, EN 570 | Profile, Tube |
Technological properties
| Property | ||
|---|---|---|
| Workability | Good workability. | |
Metal
- DIN 1725-1 Grade 3.3308 F – Premium Aluminum‑Magnesium Alloy for High‑Gloss Applications
- DIN 1725-1 Grade 3.3317 H14 – Premium Aluminum-Magnesium Alloy for High-Gloss Finishes
- DIN 1725-1 Grade 3.3317 H18 – High-Gloss Aluminum Alloy for Premium Finishes
- DIN 1725-1 Grade 3.0526 T6 Aluminum Alloy – High Strength & Corrosion Resistance
- DIN 1725‑1 Grade 3.3317 H1x – Premium High‑Gloss Aluminium Alloy
- DIN 1725-1 Grade 3.3317 H22 – Premium Al99.85Mg1 Alloy for High‑Gloss Finishes
- DIN 1725-1 Grade 3.3317 H24 – Premium Al99.85Mg1 Aluminum‑Magnesium Alloy
- DIN 1725-1 Grade 3.3317 H28: Premium Aluminum-Magnesium Alloy for High-Gloss Applications
- DIN 1725-1 Grade 3.3307 F: Premium 99.85% Al + 0.5% Mg Alloy for High-Gloss Finishes
- DIN 1725-1 Grade 3.3317 O – Premium Aluminum Alloy for Superior Gloss Finish