DIN 5512-1 S235J2G3 Steel – Normalized & Formed (N) for Structural Use
DIN S235J2G3 is a low carbon steel primary for structural use. For european steel standards DIN S235J2G3 (DIN/EN 1.0116) was replaced by the steel grade EN S235J2 (DIN/EN 1.0117) according to EN 10025 (1994-03).
Properties
General
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Density | 20 °C | 7.85 g/cm³ | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Elastic modulus | -100 °C | 217 GPa | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar | |
20 °C | 212 GPa | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar | ||
100 °C | 207 GPa | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar | ||
200 °C | 199 GPa | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar | ||
300 °C | 192 GPa | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar | ||
400 °C | 184 GPa | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar | ||
500 °C | 175 GPa | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar | ||
600 °C | 164 GPa | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar | ||
Elongation | 20 °C | 15 % | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat | A80 Transverse |
20 °C | 16 % | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat | A80 Transverse | |
20 °C | 17 % | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat | A80 Transverse | |
20 °C | 17 % | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire | A80 | |
20 °C | 18 % | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat | A80 Transverse | |
20 °C | 18 % | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire | A80 | |
20 °C | 19 % | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat | A80 Transverse | |
20 °C | 19 % | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire | A80 | |
20 °C | 20 % | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire | A80 | |
20 °C | 21 % | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat | Transverse | |
20 °C | 21 % | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Flat, Bar | ||
20 °C | 21 % | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire | A80 | |
20 °C | 22 % | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat | Transverse | |
20 °C | 22 % | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Flat, Bar | ||
20 °C | 23 % | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat | Transverse | |
20 °C | 24 % | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat | Transverse | |
20 °C | 24 % | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Flat, Bar | ||
20 °C | 25 % | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat | ||
20 °C | 26 % | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire | ||
Poisson's ratio | 20 °C | 0.284 [-] | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar | |
Shear modulus | 82 GPa | Typical for Low Carbon Steel | ||||
Tensile strength | 20 °C | 320 - 470 MPa | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Flat, Bar | |
20 °C | 340 - 470 MPa | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar | ||
20 °C | 340 - 510 MPa | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire | ||
20 °C | 360 - 510 MPa | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire | ||
20 °C | 360 - 470 MPa | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire | ||
Yield strength | 20 °C | 175 MPa | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Flat, Bar | |
20 °C | 185 MPa | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Flat, Bar | ||
20 °C | 195 MPa | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Flat, Bar | ||
20 °C | 215 MPa | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Bar | ||
20 °C | 225 MPa | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat | ||
20 °C | 235 MPa | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Coefficient of thermal expansion | -100 °C | 1.08e-05 1/K | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar | |
20 °C | 1.19e-05 1/K | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar | ||
100 °C | 1.25e-05 1/K | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar | ||
200 °C | 1.3e-05 1/K | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar | ||
300 °C | 1.36e-05 1/K | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar | ||
400 °C | 1.41e-05 1/K | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar | ||
500 °C | 1.45e-05 1/K | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar | ||
600 °C | 1.49e-05 1/K | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar | ||
Max service temperature | 500 °C | Typical for Carbon Steel | ||||
Melting point | 1480 - 1526 °C | Typical for Low Carbon Steel | ||||
Specific heat capacity | -100 °C | 423 J/(kg·K) | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar | |
20 °C | 461 J/(kg·K) | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar | ||
100 °C | 479 J/(kg·K) | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar | ||
200 °C | 499 J/(kg·K) | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar | ||
300 °C | 517 J/(kg·K) | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar | ||
400 °C | 536 J/(kg·K) | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar | ||
500 °C | 558 J/(kg·K) | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar | ||
600 °C | 587 J/(kg·K) | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar | ||
Thermal conductivity | 20 °C | 56.9 W/(m·K) | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar | |
100 °C | 56.4 W/(m·K) | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar | ||
200 °C | 53.5 W/(m·K) | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar | ||
300 °C | 49.4 W/(m·K) | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar | ||
400 °C | 45.2 W/(m·K) | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar | ||
500 °C | 41.3 W/(m·K) | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar | ||
600 °C | 37.6 W/(m·K) | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar | ||
Thermal diffusivity | 20 °C | 15.7 mm²/s | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar | |
100 °C | 14.5 mm²/s | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar | ||
200 °C | 12.9 mm²/s | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar | ||
300 °C | 11.2 mm²/s | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar | ||
400 °C | 9.6 mm²/s | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar | ||
500 °C | 7.9 mm²/s | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar | ||
600 °C | 6.3 mm²/s | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar |
Electrical
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Electrical resistivity | 20 °C | 1.83e-07 Ω·m | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar |
100 °C | 2.27e-07 Ω·m | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar | |
200 °C | 2.95e-07 Ω·m | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar | |
300 °C | 3.8e-07 Ω·m | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar | |
400 °C | 4.81e-07 Ω·m | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar | |
500 °C | 5.99e-07 Ω·m | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar | |
600 °C | 7.38e-07 Ω·m | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar |
Magnetic
| Property | Value | Comment |
|---|---|---|
Curie temperature | 770 °C | Typical for Low Carbon Steel |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Carbon | 0.17 | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar |
Manganese | 1.4 | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar |
Phosphorus | 0.035 | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar |
Sulfur | 0.035 | normalized or normalized formed (+N) | EN 10025, DIN 5512-1 | Sheet, Strip, Flat, Wire, Bar |
Metal
- DIN 2394-2: Grade St 28 Steel – Normalized & Normalized Formed (+N) Properties
- S355J2G3CuC Steel (DIN 5512-1) – Normalized/Normalized Formed for Rail Vehicle Engineering
- DIN 17240 Grade C35 Steel – Normalized or Normalized‑Formed (+N) for Creep Resistance up to 400 °C
- DIN 5512‑1 Grade S235J2W: Normalized or Normalized‑Formed Steel for Rail Vehicle Engineering
- Premium DIN 5512-1 Grade S355J2G3Cu Steel – Optimized for Rail Vehicle Engineering
- DIN 5512‑1 Grade S235J2G3Cu Steel – Normalized/Normalized‑Formed (N) for Rail Vehicle Engineering
- DIN 5512-1 Grade S235JRG2C: Normalized/Normalized Formed Steel for Rail Vehicle Engineering
- S355J2G3C Steel (DIN 5512-1) – Normalized or Normalized‑Formed (N) Specifications
- DIN 5512‑1 S235JRG2 Steel – Normalized & Normalized‑Formed (Grade +N)
- DIN 5512-1: Grade S355J2G3 Normalized/Normalized Formed – High-Strength, Corrosion-Resistant Structural Steel