DIN 5512‑1 S235JRG2 Steel – Normalized & Normalized‑Formed (Grade +N)

The steel is used for rail vehicle engineering acc. to the selected standard DIN 5512-1. The corresponding properties of EN 10025-2 shall be taken.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.85 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

212 GPa

100.0 °C

207 GPa

200.0 °C

199 GPa

300.0 °C

192 GPa

400.0 °C

184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Elongation

20.0 °C

21 - 26 %

Elongation A80

20.0 °C

17 - 21 %

Elongation A80, transverse

20.0 °C

15 - 19 %

Elongation, transverse

20.0 °C

21 - 24 %

Poisson's ratio

20.0 °C

0.28 [-]

Shear modulus

23.0 °C

82 GPa

Typical for Low Carbon Steel

Tensile strength

20.0 °C

340 - 510 MPa

Yield strength

20.0 °C

175 - 235 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.08E-5 1/K

20.0 °C

1.19E-5 1/K

100.0 °C

1.25E-5 1/K

200.0 °C

1.3E-5 1/K

300.0 °C

1.36E-5 1/K

400.0 °C

1.41E-5 1/K

500.0 °C

1.45E-5 1/K

600.0 °C

1.49E-5 1/K

Max service temperature

500 °C

Typical for Carbon Steel

Melting point

1480 - 1526 °C

Typical for Low Carbon Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

56.9 W/(m·K)

100.0 °C

56.4 W/(m·K)

200.0 °C

53.5 W/(m·K)

300.0 °C

49.4 W/(m·K)

400.0 °C

45.2 W/(m·K)

500.0 °C

41.3 W/(m·K)

600.0 °C

37.6 W/(m·K)

Thermal diffusivity

20.0 °C

15.7 mm²/s

100.0 °C

14.5 mm²/s

200.0 °C

12.9 mm²/s

300.0 °C

11.2 mm²/s

400.0 °C

9.6 mm²/s

500.0 °C

7.9 mm²/s

600.0 °C

6.3 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

1.83E-7 Ω·m

100.0 °C

2.27E-7 Ω·m

200.0 °C

2.95E-7 Ω·m

300.0 °C

3.8E-7 Ω·m

400.0 °C

4.81E-7 Ω·m

500.0 °C

5.99E-7 Ω·m

600.0 °C

7.38E-7 Ω·m

Magnetic

PropertyValueComment

Curie temperature

770 °C

Typical for Low Carbon Steel

Chemical properties

PropertyValue

Carbon

0.17 %

Copper

0.55 %

Manganese

1.4 %

Nitrogen

0.01 %

Phosphorus

0.04 %

Sulfur

0.035 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. DIN 2394-2: Grade St 28 Steel – Normalized & Normalized Formed (+N) Properties
    2. S355J2G3CuC Steel (DIN 5512-1) – Normalized/Normalized Formed for Rail Vehicle Engineering
    3. DIN 17240 Grade C35 Steel – Normalized or Normalized‑Formed (+N) for Creep Resistance up to 400 °C
    4. DIN 5512‑1 Grade S235J2W: Normalized or Normalized‑Formed Steel for Rail Vehicle Engineering
    5. Premium DIN 5512-1 Grade S355J2G3Cu Steel – Optimized for Rail Vehicle Engineering
    6. DIN 5512‑1 Grade S235J2G3Cu Steel – Normalized/Normalized‑Formed (N) for Rail Vehicle Engineering
    7. DIN 5512-1 Grade S235JRG2C: Normalized/Normalized Formed Steel for Rail Vehicle Engineering
    8. S355J2G3C Steel (DIN 5512-1) – Normalized or Normalized‑Formed (N) Specifications
    9. DIN 5512-1 S235J2G3 Steel – Normalized & Formed (N) for Structural Use
    10. DIN 5512-1: Grade S355J2G3 Normalized/Normalized Formed – High-Strength, Corrosion-Resistant Structural Steel