EN AW-5052 H19 Aluminum Alloy – Superior Corrosion Resistance & Welding Performance
Aluminum EN AW-5052 is a non-heat treatable alloy with excellent finishing qualities. EN AW-5052 offers better corrosion resistance than most aluminum alloys, especially to salt water and marine atmospheres. This alloy can be readily welded using most common techniques and is in fact offers some of the best welding characteristics of all aluminum alloys.
Properties
General
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Density | 2.68 g/cm³ | H19 | EN 573-3, EN 541 | Strip, Sheet, Plate, Foil, Wire, Tube, Bar | |
20.0 °C | 2.68 g/cm³ | H19 | EN 573-3 | Sheet | |
20.0 °C | 2.68 - 2.69 g/cm³ | H19 | EN 573-3 | Sheet | |
20.0 °C | 2.69 g/cm³ | H19 | EN 573-3 | Sheet |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Elastic modulus | 70.0 GPa | H19 | EN 573-3, EN 541 | Strip, Sheet, Plate, Foil, Wire, Tube, Bar | ||
20.0 °C | 70.0 GPa | H19 | EN 573-3 | Sheet | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||||
Poisson's ratio | 20.0 °C | 0.33 [-] | H19 | EN 573-3 | Sheet | |
Shear modulus | 26.3 GPa | H19 | EN 573-3, EN 541 | Strip, Sheet, Plate, Foil, Wire, Tube, Bar | ||
20.0 °C | 26.3 - 27.0 GPa | H19 | EN 573-3 | Sheet | ||
20.0 °C | 26.3 GPa | H19 | EN 573-3 | Sheet | ||
Tensile strength | 20.0 °C | 280.0 - 360.0 MPa | H19 | EN 573-3 | Sheet | |
20.0 °C | 280.0 - 330.0 MPa | H19 | EN 573-3 | Sheet | ||
20.0 °C | 300.0 - 360.0 MPa | H19 | EN 573-3, EN 541 | Strip, Sheet, Plate, Foil, Wire, Tube, Bar | ||
20.0 °C | 300.0 - 330.0 MPa | H19 | EN 573-3 | Sheet |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Coefficient of thermal expansion | -50.0 °C | 2.21e-05 1/K | H19 | EN 573-3 | Sheet | |
-50 °C | 2.2100000000000002e-05 1/K | H19 | EN 573-3, EN 541 | Strip, Sheet, Plate, Foil, Wire, Tube, Bar | ||
20 °C | 2.2100000000000002e-05 1/K | H19 | EN 573-3, EN 541 | Strip, Sheet, Plate, Foil, Wire, Tube, Bar | ||
20 °C | 2.38e-05 1/K | H19 | EN 573-3, EN 541 | Strip, Sheet, Plate, Foil, Wire, Tube, Bar | ||
20 °C | 2.48e-05 1/K | H19 | EN 573-3, EN 541 | Strip, Sheet, Plate, Foil, Wire, Tube, Bar | ||
20 °C | 2.5699999999999998e-05 1/K | H19 | EN 573-3, EN 541 | Strip, Sheet, Plate, Foil, Wire, Tube, Bar | ||
100 °C | 2.38e-05 1/K | H19 | EN 573-3, EN 541 | Strip, Sheet, Plate, Foil, Wire, Tube, Bar | ||
100.0 °C | 2.38e-05 1/K | H19 | EN 573-3, EN 541 | Strip, Sheet, Plate, Foil, Wire, Tube, Bar | ||
200 °C | 2.48e-05 1/K | H19 | EN 573-3, EN 541 | Strip, Sheet, Plate, Foil, Wire, Tube, Bar | ||
200.0 °C | 2.48e-05 1/K | H19 | EN 573-3, EN 541 | Strip, Sheet, Plate, Foil, Wire, Tube, Bar | ||
300 °C | 2.5699999999999998e-05 1/K | H19 | EN 573-3, EN 541 | Strip, Sheet, Plate, Foil, Wire, Tube, Bar | ||
300.0 °C | 2.57e-05 1/K | H19 | EN 573-3 | Sheet | ||
Max service temperature | 150.0 °C | Typical for Wrought 5000 Series Aluminium | ||||
Melting point | 605.0 - 650.0 °C | H19 | EN 573-3, EN 541 | Strip, Sheet, Plate, Foil, Wire, Tube, Bar | ||
607.0 - 649.0 °C | H19 | EN 573-3, EN 541 | Strip, Sheet, Plate, Foil, Wire, Tube, Bar | |||
Specific heat capacity | 900.0 J/(kg·K) | H19 | EN 573-3, EN 541 | Strip, Sheet, Plate, Foil, Wire, Tube, Bar | ||
20.0 °C | 900.0 J/(kg·K) | H19 | EN 573-3 | Sheet | ||
20.0 °C | 900.0 - 901.0 J/(kg·K) | H19 | EN 573-3 | Sheet | ||
20.0 °C | 901.0 J/(kg·K) | H19 | EN 573-3 | Sheet | ||
Thermal conductivity | 138 W/(m·K) | H19 | EN 573-3, EN 541 | Strip, Sheet, Plate, Foil, Wire, Tube, Bar | ||
20.0 °C | 130.0 - 150.0 W/(m·K) | H19 | EN 573-3, EN 541 | Strip, Sheet, Plate, Foil, Wire, Tube, Bar | ||
20.0 °C | 130.0 - 138.0 W/(m·K) | H19 | EN 573-3 | Sheet | ||
20.0 °C | 138.0 - 150.0 W/(m·K) | H19 | EN 573-3 | Sheet | ||
20.0 °C | 138.0 W/(m·K) | H19 | EN 573-3 | Sheet |
Electrical
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Electrical conductivity | 20000000.0 S/m | H19 | EN 573-3, EN 541 | Strip, Sheet, Plate, Foil, Wire, Tube, Bar | |
20.0 °C | 19000000.0 - 21000000.0 S/m | H19 | EN 573-3, EN 541 | Strip, Sheet, Plate, Foil, Wire, Tube, Bar | |
Electrical resistivity | 4.76e-08 - 5.26e-08 Ω·m | H19 | EN 573-3, EN 541 | Strip, Sheet, Plate, Foil, Wire, Tube, Bar | |
5e-08 Ω·m | H19 | EN 573-3, EN 541 | Strip, Sheet, Plate, Foil, Wire, Tube, Bar | ||
20.0 °C | 4.7e-08 - 4.95e-08 Ω·m | H19 | EN 573-3 | Sheet | |
20.0 °C | 4.7e-08 - 5.2e-08 Ω·m | H19 | EN 573-3 | Sheet | |
20.0 °C | 4.95e-08 Ω·m | H19 | EN 573-3 | Sheet | |
20.0 °C | 4.95e-08 - 5.2e-08 Ω·m | H19 | EN 573-3 | Sheet |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chromium | 0.15 - 0.35 % | H19 | EN 573-3, EN 541 | Sheet, Strip, Plate, Foil, Wire, Tube, Bar |
Copper | 0.1 % | H19 | EN 573-3, EN 541 | Sheet, Strip, Plate, Foil, Wire, Tube, Bar |
Iron | 0.4 % | H19 | EN 573-3 | Sheet |
0.40 % | H19 | EN 573-3, EN 541 | Strip, Sheet, Plate, Foil, Wire, Tube, Bar | |
Magnesium | 2.2 - 2.8 % | H19 | EN 573-3, EN 541 | Sheet, Strip, Plate, Foil, Wire, Tube, Bar |
Manganese | 0.1 % | H19 | EN 573-3, EN 541 | Sheet, Strip, Plate, Foil, Wire, Tube, Bar |
Silicon | 0.25 % | H19 | EN 573-3, EN 541 | Sheet, Strip, Plate, Foil, Wire, Tube, Bar |
Zinc | 0.1 % | H19 | EN 573-3, EN 541 | Sheet, Strip, Plate, Foil, Wire, Tube, Bar |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | decorative: good, Protective: very good | |
| Corrosion properties | Seawater: very good to good, weathering: good | |
| Workability | Bending / Spinning (cold): very good / acceptable, Impact extrusion (cold): acceptable, Deep drawing / upsetting (Condition) good (O) / good (H12) | |
Metal
- EN 573-3 Grade 3.0506 H19 – Premium Lean Aluminum Alloy for Marine & Thermal Applications
- EN AW-5052 H47 Aluminum Alloy – Superior Corrosion Resistance & Weldability
- EN 573-3 AW-5052 H25 Aluminum Alloy: Superior Corrosion Resistance & Weldability
- EN 573-3 AW-5052 H45 Aluminum Alloy – High Corrosion Resistance & Superior Welding
- EN 573-3 Grade 3.0517 H19 – Superior Corrosion‑Resistant Aluminum Alloy
- EN 573-3 Grade AW-5052 H42 Aluminum – Superior Corrosion Resistance & Weldability
- EN AW-5052 H44 Aluminum Alloy – Grade EN 573-3, Corrosion‑Resistant & Weldable
- EN 573-3 AW-5052 F: Premium Aluminum Alloy for Superior Corrosion Resistance
- EN 573-3 Grade AW-5052 H48 – Superior Corrosion‑Resistant Aluminum Alloy for Marine Applications
- EN 573-3 Grade AW‑5052 H46: Premium Marine-Grade Aluminum Alloy