EN 573-3 Grade 3.3547 H111 – High-Strength Steel Properties

Properties

General

Property	Value	Condition	Related Standards
Density	2.66 g/cm³	H111	EN 573-3, EN 14286, EN 485, EN 754, EN 755

Mechanical

Property	Value	Condition	Related Standards	Comment
Bending angle 180°	1.0 °/t	H111	EN 573-3, EN 485
	1.5 °/t	H111	EN 573-3, EN 14286, EN 485
	4.0 °/t	H111	EN 573-3, EN 14286
Bending angle 90°	0.5 °/t	H111	EN 573-3, EN 485
	1.0 °/t	H111	EN 573-3, EN 485
	1.5 °/t	H111	EN 573-3, EN 485
	2.5 °/t	H111	EN 573-3, EN 485
Elastic modulus	71.0 GPa	H111	EN 573-3, EN 14286, EN 485, EN 754, EN 755
Hardness, Brinell	69.0 [-]	H111	EN 573-3, EN 485
	70.0 [-]	H111	EN 573-3, EN 485
	73.0 [-]	H111	EN 573-3, EN 485
	75.0 [-]	H111	EN 573-3, EN 485
Plane-Strain Fracture Toughnes	22.0 - 35.0 MPa·√m			Typical for Wrought 5000 Series Aluminium
Poisson's ratio	0.33 [-]			Typical for Wrought 5000 Series Aluminium
Shear modulus	26.8 GPa	H111	EN 573-3, EN 14286, EN 485, EN 754, EN 755
Tensile strength	245.0 MPa	H111	EN 573-3, EN 485
	250.0 MPa	H111	EN 573-3, EN 485
	255.0 MPa	H111	EN 573-3, EN 485
	260.0 MPa	H111	EN 573-3, EN 485
	270.0 - 345.0 MPa	H111	EN 573-3, EN 485
	270.0 - 350.0 MPa	H111	EN 573-3, EN 754
	270.0 MPa	H111	EN 573-3, EN 755
	275.0 - 350.0 MPa	H111	EN 573-3, EN 485
	290.0 - 370.0 MPa	H111	EN 573-3, EN 14286

Thermal

Property	Temperature	Value	Condition	Related Standards	Comment
Coefficient of thermal expansion	-50 °C	2.23e-05 1/K	H111	EN 573-3, EN 14286, EN 485, EN 754, EN 755
	20 °C	2.23e-05 1/K	H111	EN 573-3, EN 14286, EN 485, EN 754, EN 755
	20 °C	2.42e-05 1/K	H111	EN 573-3, EN 14286, EN 485, EN 754, EN 755
	20 °C	2.4999999999999998e-05 1/K	H111	EN 573-3, EN 14286, EN 485, EN 754, EN 755
	20 °C	2.6e-05 1/K	H111	EN 573-3, EN 14286, EN 485, EN 754, EN 755
	100 °C	2.42e-05 1/K	H111	EN 573-3, EN 14286, EN 485, EN 754, EN 755
	200 °C	2.4999999999999998e-05 1/K	H111	EN 573-3, EN 14286, EN 485, EN 754, EN 755
	300 °C	2.6e-05 1/K	H111	EN 573-3, EN 14286, EN 485, EN 754, EN 755
Max service temperature		150.0 °C			Typical for Wrought 5000 Series Aluminium
Melting point		574.0 - 638.0 °C	H111	EN 573-3, EN 14286, EN 485, EN 754, EN 755
Specific heat capacity		900.0 J/(kg·K)	H111	EN 573-3, EN 14286, EN 485, EN 754, EN 755
Thermal conductivity		110.0 - 140.0 W/(m·K)	H111	EN 573-3, EN 14286, EN 485, EN 754, EN 755

Electrical

Property	Value	Condition	Related Standards
Electrical conductivity	16000000.0 - 19000000.0 S/m	H111	EN 573-3, EN 14286, EN 485, EN 754, EN 755
Electrical resistivity	5.26e-08 - 6.25e-08 Ω·m	H111	EN 573-3, EN 14286, EN 485, EN 754, EN 755

Chemical properties

Property	Value	Condition	Related Standards
Chromium	0.05 - 0.25 %	H111	EN 573-3, EN 14286, EN 485, EN 754, EN 755
Copper	0.1 %	H111	EN 573-3, EN 14286, EN 485, EN 754, EN 755
Iron	0.40 %	H111	EN 573-3, EN 14286, EN 485, EN 754, EN 755
Magnesium	4.0 - 4.9 %	H111	EN 573-3, EN 14286, EN 485, EN 754, EN 755
Manganese	0.4 - 1.0 %	H111	EN 573-3, EN 14286, EN 485, EN 754, EN 755
Silicon	0.4 %	H111	EN 573-3, EN 14286, EN 485, EN 754, EN 755
Titanium	0.15 %	H111	EN 573-3, EN 14286, EN 485, EN 754, EN 755
Zinc	0.25 %	H111	EN 573-3, EN 14286, EN 485, EN 754, EN 755

Technological properties

Property
Anodizing	decorative: sufficient, Protective: good
Brazing	hard brazing (with flux/ without flux): poor / poor, friction soldering: acceptable, soft brazing with flux: poor
Corrosion properties	Seawater: very good, weathering: very good
Workability	Bending / Spinning (cold): good / sufficient, Impact extrusion (cold): sufficient, Deep drawing / upsetting (Condition) good (O) / good (O)

Metal