EN 1706 Grade AC-43200 T6 Aluminium Alloy – High Strength & Reliability for Precision Casting
Aluminium casting alloy (sand casting, permanent mould casting)
Properties
General
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Density | 2.65 g/cm³ | T6 | EN 1706 | Casting | |
20.0 °C | 2.65 g/cm³ | T6 | EN 1706 |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Bending Fatigue Strength | 80.0 - 110.0 MPa | T6 | EN 1706 | Casting | ||
Elastic modulus | 74.0 GPa | T6 | EN 1706 | Casting | ||
20.0 °C | 74.0 GPa | T6 | EN 1706 | |||
Hardness, Brinell | 75.0 [-] | T6 | EN 1706 | Casting | ||
80.0 [-] | T6 | EN 1706 | Casting | |||
20.0 °C | 75.0 [-] | T6 | EN 1706 | |||
20.0 °C | 80.0 [-] | T6 | EN 1706 | |||
Poisson's ratio | 0.33 [-] | Typical for Cast 3xx.x Series Aluminium | ||||
Shear modulus | 2.8 GPa | Typical for Cast 3xx.x Series Aluminium | ||||
Tensile strength | 220.0 MPa | T6 | EN 1706 | Casting | ||
240.0 MPa | T6 | EN 1706 | Casting | |||
20.0 °C | 220.0 MPa | T6 | EN 1706 | |||
20.0 °C | 240.0 MPa | T6 | EN 1706 |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.1e-05 1/K | T6 | EN 1706 | Casting |
100.0 °C | 2.1e-05 1/K | T6 | EN 1706 | Casting | |
100 °C | 2.1e-05 1/K | T6 | EN 1706 | Casting | |
Melting point | 530.0 - 600.0 °C | T6 | EN 1706 | Casting | |
Specific heat capacity | 900.0 J/(kg·K) | T6 | EN 1706 | Casting | |
20.0 °C | 900.0 J/(kg·K) | T6 | EN 1706 | ||
Thermal conductivity | 20.0 °C | 130.0 - 170.0 W/(m·K) | T6 | EN 1706 | Casting |
Electrical
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Electrical conductivity | 20.0 °C | 16000000.0 - 24000000.0 S/m | T6 | EN 1706 | Casting |
Electrical resistivity | 4.17e-08 - 6.25e-08 Ω·m | T6 | EN 1706 | Casting |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Aluminium | 86.05 % | T6 | EN 1706 | |
Copper | 0.35 % | T6 | EN 1706 | Casting |
Iron | 0.65 % | T6 | EN 1706 | |
0.65 % | T6 | EN 1706 | Casting | |
Lead | 0.1 % | T6 | EN 1706 | Casting |
Magnesium | 0.2 - 0.45 % | T6 | EN 1706 | Casting |
Manganese | 0.55 % | T6 | EN 1706 | Casting |
Nickel | 0.15 % | T6 | EN 1706 | Casting |
Silicon | 9.0 - 11.0 % | T6 | EN 1706 | Casting |
Titanium | 0.2 % | T6 | EN 1706 | Casting |
Zinc | 0.35 % | T6 | EN 1706 | Casting |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | decorative: not recommended | |
| Corrosion properties | general: acceptable | |
| General machinability | after thermal treatment: good to acceptable, as cast: good | |
| Processing methods | permanent mould casting, separately cast test sample | |
Metal
- EN 1706 Grade AC-21000 T4 Aluminium Casting Alloy – Key Properties & Standards
- EN 1706 Grade AC-21100 T6 Aluminium Casting Alloy – Properties & Specifications
- EN 1706 AC-21100 T64 Aluminium Casting Alloy – Specifications & Properties
- EN 1706 AC-44000 F Aluminium Casting Alloy – Key Properties & Standards
- EN 1706 Grade AC-44100 F – High-Performance Aluminium Casting Alloy
- EN 1706 Grade AC-44200 F Aluminium Casting Alloy – High-Performance, Industrial Grade
- EN 1706 AC-44300 F Aluminium Casting Alloy – Key Properties & Standards
- EN 1706 AC-44400F Aluminium Casting Alloy – Key Properties & Standards
- EN 1706 AC-43200F – Premium Aluminium Casting Alloy for High-Performance Applications
- EN 1706 Grade AC-45000 F Aluminium Casting Alloy – Key Properties & Standards