EN 1706 Grade AC-45300 T4: Key Properties of Aluminium Casting Alloy
Aluminium casting alloy (sand casting, permanent mould casting)
Properties
General
| Property | Value | Comment |
|---|---|---|
Density | 2.65 - 2.7 g/cm³ | Typical for Cast 3xx.x Series Aluminium |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Bending Fatigue Strength | 70.0 - 100.0 MPa | T4 | EN 1706 | Casting | ||
Elastic modulus | 73.0 - 80.0 GPa | Typical for Cast 3xx.x Series Aluminium | ||||
Hardness, Brinell | 80.0 [-] | T4 | EN 1706 | Casting | ||
85.0 [-] | T4 | EN 1706 | Casting | |||
20.0 °C | 80.0 [-] | T4 | EN 1706 | |||
20.0 °C | 85.0 [-] | T4 | EN 1706 | |||
Poisson's ratio | 0.33 [-] | Typical for Cast 3xx.x Series Aluminium | ||||
Shear modulus | 2.8 GPa | Typical for Cast 3xx.x Series Aluminium | ||||
Tensile strength | 170.0 MPa | T4 | EN 1706 | Casting | ||
230.0 MPa | T4 | EN 1706 | Casting | |||
20.0 °C | 170.0 MPa | T4 | EN 1706 | |||
20.0 °C | 230.0 MPa | T4 | EN 1706 |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.2e-05 1/K | T4 | EN 1706 | Casting | |
100.0 °C | 2.2e-05 1/K | T4 | EN 1706 | Casting | ||
100 °C | 2.2e-05 1/K | T4 | EN 1706 | Casting | ||
Melting point | 505.0 - 770.0 °C | Typical for Cast 3xx.x Series Aluminium | ||||
Specific heat capacity | 960.0 - 963.0 J/(kg·K) | Typical for Cast 3xx.x Series Aluminium | ||||
Thermal conductivity | 20.0 °C | 140.0 - 150.0 W/(m·K) | T4 | EN 1706 | Casting |
Electrical
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Electrical conductivity | 20.0 °C | 19000000.0 - 23000000.0 S/m | T4 | EN 1706 | Casting |
Electrical resistivity | 4.35e-08 - 5.26e-08 Ω·m | T4 | EN 1706 | Casting |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Aluminium | 90.15 % | T4 | EN 1706 | |
Copper | 1.0 - 1.5 % | T4 | EN 1706 | Casting |
Iron | 0.65 % | T4 | EN 1706 | |
0.65 % | T4 | EN 1706 | Casting | |
Lead | 0.15 % | T4 | EN 1706 | Casting |
Magnesium | 0.35 - 0.65 % | T4 | EN 1706 | Casting |
Manganese | 0.55 % | T4 | EN 1706 | Casting |
Nickel | 0.25 % | T4 | EN 1706 | Casting |
Silicon | 4.5 - 5.5 % | T4 | EN 1706 | Casting |
Tin | 0.05 % | T4 | EN 1706 | Casting |
Titanium | 0.05 - 0.25 % | T4 | EN 1706 | Casting |
Zinc | 0.15 % | T4 | EN 1706 | Casting |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | decorative: not sufficient | |
| Corrosion properties | general: not sufficient | |
| General machinability | after thermal treatment: good, as cast: good | |
| Processing methods | permanent mould casting, separately cast test sample | |
Metal
- EN 1706 AC-44000 F Aluminium Casting Alloy – Key Properties & Standards
- EN 1706 Grade AC-44100 F – High-Performance Aluminium Casting Alloy
- EN 1706 Grade AC-44200 F Aluminium Casting Alloy – High-Performance, Industrial Grade
- EN 1706 AC-44300 F Aluminium Casting Alloy – Key Properties & Standards
- EN 1706 AC-44400F Aluminium Casting Alloy – Key Properties & Standards
- EN 1706 AC-51200 F Aluminium Casting Alloy – Key Properties & Standards
- EN 1706 Grade AC-51300 F – High-Strength Aluminium Casting Alloy
- EN 1706 AC-46500 F – Aluminium Die Casting Alloy: Properties & Standards
- EN 1706 AC‑46600 F Aluminium Alloy – High‑Strength, Low‑Density Casting Solution
- EN 1706 AC-45300 T6 Aluminium Casting Alloy – Properties & Standards