EN 573-3 Grade 3.1355 H111 – High-Strength Aluminum Alloy for Aerospace Applications

Aluminum DIN 3.1355, known for its use in aircraft industry, is an alloy that offers excellent strength. When in the annealed condition it is readily formed and has good machinability. Though it has a relatively low level of corrosion resistance, it can be machined to a high finish.

Properties

General

Property	Value	Condition	Related Standards
Density	2.77 g/cm³	H111	EN 573-3, EN 754, EN 755
	2.78 g/cm³	H111	EN 573-3, EN 754, EN 755

Mechanical

Property	Value	Condition	Related Standards	Comment
Elastic modulus	73.0 GPa	H111	EN 573-3, EN 754, EN 755
Plane-Strain Fracture Toughnes	22.0 - 35.0 MPa·√m			Typical for Wrought 2000 Series Aluminium
Poisson's ratio	0.33 [-]			Typical for Wrought 2000 Series Aluminium
Shear modulus	27.4 GPa	H111	EN 573-3, EN 754, EN 755
Tensile strength	240.0	H111	EN 573-3, EN 754
	250.0	H111	EN 573-3, EN 754, EN 755

Thermal

Property	Temperature	Value	Condition	Related Standards
Coefficient of thermal expansion	-50 °C	2.11e-05 1/K	H111	EN 573-3, EN 754, EN 755
	20 °C	2.11e-05 1/K	H111	EN 573-3, EN 754, EN 755
	20 °C	2.2899999999999998e-05 1/K	H111	EN 573-3, EN 754, EN 755
	20 °C	2.3199999999999998e-05 1/K	H111	EN 573-3, EN 754, EN 755
	20 °C	2.38e-05 1/K	H111	EN 573-3, EN 754, EN 755
	20 °C	2.4699999999999997e-05 1/K	H111	EN 573-3, EN 754, EN 755
	100 °C	2.2899999999999998e-05 1/K	H111	EN 573-3, EN 754, EN 755
	100 °C	2.3199999999999998e-05 1/K	H111	EN 573-3, EN 754, EN 755
	200 °C	2.38e-05 1/K	H111	EN 573-3, EN 754, EN 755
	300 °C	2.4699999999999997e-05 1/K	H111	EN 573-3, EN 754, EN 755
Melting point		505.0 - 640.0 °C	H111	EN 573-3, EN 754, EN 755
		505.0 - 635.0 °C	H111	EN 573-3, EN 754, EN 755
Specific heat capacity		875.0 J/(kg·K)	H111	EN 573-3, EN 754, EN 755
Thermal conductivity		121.0 - 193.0 W/(m·K)	H111	EN 573-3, EN 754, EN 755
		130.0 - 150.0 W/(m·K)	H111	EN 573-3, EN 754, EN 755

Electrical

Property	Value	Condition	Related Standards
Electrical conductivity	17000000.0 - 29000000.0 S/m	H111	EN 573-3, EN 754, EN 755
	18000000.0 - 21000000.0 S/m	H111	EN 573-3, EN 754, EN 755
Electrical resistivity	3.45e-08 - 5.88e-08 Ω·m	H111	EN 573-3, EN 754, EN 755
	4.76e-08 - 5.56e-08 Ω·m	H111	EN 573-3, EN 754, EN 755

Chemical properties

Property	Value	Condition	Related Standards
Chromium	0.1 %	H111	EN 573-3, EN 754, EN 755
Copper	3.8 - 4.9 %	H111	EN 573-3, EN 754, EN 755
Iron	0.50 %	H111	EN 573-3, EN 754, EN 755
Magnesium	1.2 - 1.8 %	H111	EN 573-3, EN 754, EN 755
Manganese	0.3 - 0.9 %	H111	EN 573-3, EN 754, EN 755
Silicon	0.5 %	H111	EN 573-3, EN 754, EN 755
Titanium	0.15 %	H111	EN 573-3, EN 754, EN 755
Zinc	0.25 %	H111	EN 573-3, EN 754, EN 755

Technological properties

Property
Anodizing	decorative: not suitable, Protective: good
Brazing	hard brazing (with flux/ without flux): not suitable / not suitable, friction soldering: acceptable, soft brazing with flux: not suitable
Corrosion properties	Seawater: poor, weathering: poor
Workability	Bending / Spinning (cold): sufficient (O) / acceptable (O), Impact extrusion (cold): acceptable (O), Deep drawing / upsetting (Condition) acceptable (O) / sufficient (O)

DIN 1725-1 Grade 3.1305 T4 – High‑Strength Al‑Cu‑Mg Alloy EN 573-3 Grade 3.1355 T3510 Aluminum Alloy – Aircraft‑Grade Strength & Machinability