EN 573-3 Grade 3.1355 T8 Aluminum Alloy – High Strength, Excellent Machinability

Aluminum DIN 3.1355, known for its use in aircraft industry, is an alloy that offers excellent strength. When in the annealed condition it is readily formed and has good machinability. Though it has a relatively low level of corrosion resistance, it can be machined to a high finish.

Properties

General

Property	Value	Condition	Related Standards
Density	2.77 g/cm³	T8	EN 573-3, EN 485, EN 754, EN 755
	2.78 g/cm³	T8	EN 573-3, EN 485, EN 754, EN 755

Mechanical

Property	Value	Condition	Related Standards	Comment
Bending Fatigue Strength	125.0 MPa	T8	EN 573-3, EN 485, EN 754, EN 755
Bending angle 90°	5.0 °/t	T8	EN 573-3, EN 485
	7.0 °/t	T8	EN 573-3, EN 485
Elastic modulus	73.0 GPa	T8	EN 573-3, EN 485, EN 754, EN 755
Hardness, Brinell	138.0 [-]	T8	EN 573-3, EN 485
Plane-Strain Fracture Toughnes	22.0 - 35.0 MPa·√m			Typical for Wrought 2000 Series Aluminium
Poisson's ratio	0.33 [-]			Typical for Wrought 2000 Series Aluminium
Shear modulus	27.4 GPa	T8	EN 573-3, EN 485, EN 754, EN 755
Tensile strength	455.0 MPa	T8	EN 573-3, EN 754, EN 755
	460.0 MPa	T8	EN 573-3, EN 485

Thermal

Property	Temperature	Value	Condition	Related Standards
Coefficient of thermal expansion	-50 °C	2.11e-05 1/K	T8	EN 573-3, EN 485, EN 754, EN 755
	20 °C	2.11e-05 1/K	T8	EN 573-3, EN 485, EN 754, EN 755
	20 °C	2.2899999999999998e-05 1/K	T8	EN 573-3, EN 485, EN 754, EN 755
	20 °C	2.3199999999999998e-05 1/K	T8	EN 573-3, EN 485, EN 754, EN 755
	20 °C	2.38e-05 1/K	T8	EN 573-3, EN 485, EN 754, EN 755
	20 °C	2.4699999999999997e-05 1/K	T8	EN 573-3, EN 485, EN 754, EN 755
	100 °C	2.2899999999999998e-05 1/K	T8	EN 573-3, EN 485, EN 754, EN 755
	100 °C	2.3199999999999998e-05 1/K	T8	EN 573-3, EN 485, EN 754, EN 755
	200 °C	2.38e-05 1/K	T8	EN 573-3, EN 485, EN 754, EN 755
	300 °C	2.4699999999999997e-05 1/K	T8	EN 573-3, EN 485, EN 754, EN 755
Melting point		505.0 - 640.0 °C	T8	EN 573-3, EN 485, EN 754, EN 755
		505.0 - 635.0 °C	T8	EN 573-3, EN 485, EN 754, EN 755
Specific heat capacity		875.0 J/(kg·K)	T8	EN 573-3, EN 485, EN 754, EN 755
Thermal conductivity		121.0 - 193.0 W/(m·K)	T8	EN 573-3, EN 485, EN 754, EN 755
		130.0 - 150.0 W/(m·K)	T8	EN 573-3, EN 485, EN 754, EN 755

Electrical

Property	Value	Condition	Related Standards
Electrical conductivity	17000000.0 - 29000000.0 S/m	T8	EN 573-3, EN 485, EN 754, EN 755
	18000000.0 - 21000000.0 S/m	T8	EN 573-3, EN 485, EN 754, EN 755
Electrical resistivity	3.45e-08 - 5.88e-08 Ω·m	T8	EN 573-3, EN 485, EN 754, EN 755
	4.76e-08 - 5.56e-08 Ω·m	T8	EN 573-3, EN 485, EN 754, EN 755

Chemical properties

Property	Value	Condition	Related Standards
Chromium	0.1 %	T8	EN 573-3, EN 485, EN 754, EN 755
Copper	3.8 - 4.9 %	T8	EN 573-3, EN 485, EN 754, EN 755
Iron	0.50 %	T8	EN 573-3, EN 485, EN 754, EN 755
Magnesium	1.2 - 1.8 %	T8	EN 573-3, EN 485, EN 754, EN 755
Manganese	0.3 - 0.9 %	T8	EN 573-3, EN 485, EN 754, EN 755
Silicon	0.5 %	T8	EN 573-3, EN 485, EN 754, EN 755
Titanium	0.15 %	T8	EN 573-3, EN 485, EN 754, EN 755
Zinc	0.25 %	T8	EN 573-3, EN 485, EN 754, EN 755

Technological properties

Property
Anodizing	decorative: not suitable, Protective: good
Brazing	hard brazing (with flux/ without flux): not suitable / not suitable, friction soldering: acceptable, soft brazing with flux: not suitable
Corrosion properties	Seawater: poor, weathering: poor
Workability	Bending / Spinning (cold): sufficient (O) / acceptable (O), Impact extrusion (cold): acceptable (O), Deep drawing / upsetting (Condition) acceptable (O) / sufficient (O)