8011A O – Non‑Heat Treatable Aluminum Wrought Alloy: Key Properties & Applications
Good formability.
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 23.0 °C | 2.71 g/cm³ |
Dimension
| Property | Value |
|---|---|
Thickness | 0.08 - 0.2 mm |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 68.6 GPa | |
Elongation A50 | 23.0 °C | 18 % | according to EN 485-2 |
Shear modulus | 23.0 °C | 25.73 GPa | |
Tensile strength | 23.0 °C | 90 - 120 MPa | according to EN 485-2 |
Yield strength | 23.0 °C | 30 - 70 MPa | according to EN 485-2 |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 100.0 °C | 2.4E-5 1/K | 20-100°C |
Thermal conductivity | 23.0 °C | 201 W/(m·K) |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical resistivity | 23.0 °C | 3E-8 - 3.5E-8 Ω·m |
Chemical properties
| Property | Value |
|---|---|
Chromium | 0.1 % |
Copper | 0.1 % |
Iron | 0.5 - 1 % |
Magnesium | 0.1 % |
Manganese | 0.1 % |
Silicon | 0.4 - 0.8 % |
Titanium | 0.05 % |
Zinc | 0.1 % |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | Good | |
| Application areas | Facades: Single sheet, Sheets for composites/ sandwich Panels, Sheets for mechanized panels; Roofing: Foil for bituminous coating; Doors: Sheets for composites/ sandwich Panels, Sheets for mechanized panels; Interiors and ceilings: Sheets for mechanized panels; Furniture, Plinths, Blinds: Intermediate transformation/interior use; Heat exchangers: Fins, General applications; Tubes: Flexible tube, Pipes; Insulation; Closures: Long cups, Short cups, Easy open; Cosmetic: Cosmetic pieces; Pharmacy: Pharma and para-pharma; Semi-rigid and corrugated: Pet food, Smooth wall; Foil stock: Foil app | |
| Corrosion properties | Moderated | |
| Welding | Excellent | |
| Workability | Excellent | |
Metal
- 5252-O: High-Purity, Non-Heat-Treatable Aluminum Wrought Alloy for Superior Brightening and Anodizing
- 1350 H19 Non-Heat-Treatable Al Wrought Alloy – High Conductivity & Mechanical Strength
- 8014 H21 – High-Strength Non-Heat-Treatable Aluminum Wrought Alloy
- 1200O Aluminum Wrought Alloy – Superior Corrosion Resistance & Workability
- 3105A H28 Non-Heat-Treatable Aluminum Alloy – Low‑to‑Medium Strength, Superior Corrosion Resistance
- High-Performance 5251 H18 Aluminum Alloy – Medium Strength, Excellent Formability & Corrosion Resistance
- 5251 H28 Non-Heat-Treatable Aluminum Wrought Alloy – High Strength & Excellent Formability
- 8011A H24 Aluminum Wrought Alloy – Non-Heat-Treatable, High Formability
- 5251 O: High-Strength, Formable Non-Heat-Treatable Aluminum Wrought Alloy
- 3103-O: High-Strength, Non-Heat-Treatable Aluminum Alloy for Structural Applications