8014 H21 – High-Strength Non-Heat-Treatable Aluminum Wrought Alloy
High strength inside the foil app compared to 1xxx. Alloy 8014 can be welded, adhesive bonded, and formed easily.
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 23.0 °C | 2.73 g/cm³ |
Dimension
| Property | Value |
|---|---|
Thickness | 0.5 - 1 mm |
Mechanical
| Property | Temperature | Value |
|---|---|---|
Elastic modulus | 23.0 °C | 69 GPa |
Elongation A50 | 23.0 °C | 25 % |
Shear modulus | 23.0 °C | 26 GPa |
Tensile strength | 23.0 °C | 90 - 120 MPa |
Yield strength | 23.0 °C | 40 - 70 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 100.0 °C | 2.4E-5 1/K | 20-100°C |
Thermal conductivity | 23.0 °C | 120 W/(m·K) |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical resistivity | 23.0 °C | 3E-8 Ω·m |
Chemical properties
| Property | Value |
|---|---|
Copper | 0.2 % |
Iron | 1.2 - 1.6 % |
Magnesium | 0.1 % |
Manganese | 0.2 - 0.6 % |
Silicon | 0.3 % |
Titanium | 0.1 % |
Zinc | 0.1 % |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | Good | |
| Application areas | Semi-rigid and corrugated: Pet food; Automotive trim: Interior trim | |
| Corrosion properties | Moderated | |
| Welding | Excellent | |
| Workability | Excellent | |
Metal
- 5252-O: High-Purity, Non-Heat-Treatable Aluminum Wrought Alloy for Superior Brightening and Anodizing
- 1350 H19 Non-Heat-Treatable Al Wrought Alloy – High Conductivity & Mechanical Strength
- 8011A O – Non‑Heat Treatable Aluminum Wrought Alloy: Key Properties & Applications
- 1200O Aluminum Wrought Alloy – Superior Corrosion Resistance & Workability
- 3105A H28 Non-Heat-Treatable Aluminum Alloy – Low‑to‑Medium Strength, Superior Corrosion Resistance
- High-Performance 5251 H18 Aluminum Alloy – Medium Strength, Excellent Formability & Corrosion Resistance
- 5251 H28 Non-Heat-Treatable Aluminum Wrought Alloy – High Strength & Excellent Formability
- 5251 H38 Aluminum Wrought Alloy – Non-Heat-Treatable, High Work Hardening & Corrosion Resistance
- 5251 O: High-Strength, Formable Non-Heat-Treatable Aluminum Wrought Alloy
- 3103-O: High-Strength, Non-Heat-Treatable Aluminum Alloy for Structural Applications