EN 573-3 Grade 3.3545 H26 Aluminum Alloy – Superior Corrosion Resistance & High Conductivity

Aluminum DIN 3.3545 is structural alloy, which offers users strong corrosion resistance and high electrical conductivity. Offering higher strength levels than 5052 or 5083, DIN 3.3545 becomes stronger with stain hardening and cold working, all while remaining a cost-effective choice. It can be welded with conventional methods, though electric arc welding is preferred.

Properties

General

Property	Value	Condition	Related Standards
Density	2.66 g/cm³	H26	EN 573-3, EN 1592, EN 485, EN 754

Mechanical

Property	Value	Condition	Related Standards	Comment
Elastic modulus	71.0 GPa	H26	EN 573-3, EN 1592, EN 485, EN 754
Hardness, Brinell	96.0 [-]	H26	EN 573-3, EN 485
Plane-Strain Fracture Toughnes	22.0 - 35.0 MPa·√m			Typical for Wrought 5000 Series Aluminium
Poisson's ratio	0.33 [-]			Typical for Wrought 5000 Series Aluminium
Shear modulus	26.7 GPa	H26	EN 573-3, EN 1592, EN 485, EN 754
Tensile strength	320.0 MPa	H26	EN 573-3, EN 1592, EN 754
	325.0 - 385.0 MPa	H26	EN 573-3, EN 485

Thermal

Property	Temperature	Value	Condition	Related Standards	Comment
Coefficient of thermal expansion	-50 °C	2.2e-05 1/K	H26	EN 573-3, EN 1592, EN 485, EN 754
	20 °C	2.2e-05 1/K	H26	EN 573-3, EN 1592, EN 485, EN 754
	20 °C	2.38e-05 1/K	H26	EN 573-3, EN 1592, EN 485, EN 754
	20 °C	2.4699999999999997e-05 1/K	H26	EN 573-3, EN 1592, EN 485, EN 754
	20 °C	2.58e-05 1/K	H26	EN 573-3, EN 1592, EN 485, EN 754
	100 °C	2.38e-05 1/K	H26	EN 573-3, EN 1592, EN 485, EN 754
	200 °C	2.4699999999999997e-05 1/K	H26	EN 573-3, EN 1592, EN 485, EN 754
	300 °C	2.58e-05 1/K	H26	EN 573-3, EN 1592, EN 485, EN 754
Max service temperature		150.0 °C			Typical for Wrought 5000 Series Aluminium
Melting point		585.0 - 641.0 °C	H26	EN 573-3, EN 1592, EN 485, EN 754
		585.0 - 640.0 °C	H26	EN 573-3, EN 1592, EN 485, EN 754
Specific heat capacity		900.0 J/(kg·K)	H26	EN 573-3, EN 1592, EN 485, EN 754
Thermal conductivity		120.0 - 140.0 W/(m·K)	H26	EN 573-3, EN 1592, EN 485, EN 754
		126 W/(m·K)	H26	EN 573-3, EN 1592, EN 485, EN 754

Electrical

Property	Value	Condition	Related Standards
Electrical conductivity	17000000.0 - 19000000.0 S/m	H26	EN 573-3, EN 1592, EN 485, EN 754
	18000000.0 S/m	H26	EN 573-3, EN 1592, EN 485, EN 754
Electrical resistivity	5.26e-08 - 5.88e-08 Ω·m	H26	EN 573-3, EN 1592, EN 485, EN 754
	5.56e-08 Ω·m	H26	EN 573-3, EN 1592, EN 485, EN 754

Chemical properties

Property	Value	Condition	Related Standards
Chromium	0.05 - 0.25 %	H26	EN 573-3, EN 1592, EN 485, EN 754
Copper	0.1 %	H26	EN 573-3, EN 1592, EN 485, EN 754
Iron	0.50 %	H26	EN 573-3, EN 1592, EN 485, EN 754
Magnesium	3.5 - 4.5 %	H26	EN 573-3, EN 1592, EN 485, EN 754
Manganese	0.2 - 0.7 %	H26	EN 573-3, EN 1592, EN 485, EN 754
Silicon	0.4 %	H26	EN 573-3, EN 1592, EN 485, EN 754
Titanium	0.15 %	H26	EN 573-3, EN 1592, EN 485, EN 754
Zinc	0.25 %	H26	EN 573-3, EN 1592, EN 485, EN 754

Technological properties

Property
Anodizing	decorative: acceptable, Protective: very good
Brazing	hard brazing (with flux/ without flux): poor / sufficient, friction soldering: acceptable, soft brazing with flux: poor
Workability	Bending / Spinning (cold): good / sufficient, Impact extrusion (cold): sufficient, Deep drawing / upsetting (Condition) good (O) / good (O)

Property

Anodizing

decorative: acceptable, Protective: very good

Brazing

hard brazing (with flux/ without flux): poor / sufficient, friction soldering: acceptable, soft brazing with flux: poor

Workability

Bending / Spinning (cold): good / sufficient, Impact extrusion (cold): sufficient, Deep drawing / upsetting (Condition) good (O) / good (O)

EN 573-3 AW-3105 H44 – Premium Aluminum‑Manganese Alloy EN 573-3 Grade 3.3545 H36 – High‑Strength, Corrosion‑Resistant Aluminum Alloy