EN 573-3 Grade 3.3545 H14 – High-Strength, Corrosion-Resistant Aluminum Alloy

Aluminum DIN 3.3545 is structural alloy, which offers users strong corrosion resistance and high electrical conductivity. Offering higher strength levels than 5052 or 5083, DIN 3.3545 becomes stronger with stain hardening and cold working, all while remaining a cost-effective choice. It can be welded with conventional methods, though electric arc welding is preferred.

Properties

General

Property	Value	Condition	Related Standards
Density	2.66 g/cm³	H14	EN 573-3, EN 1592, EN 485, EN 754

Mechanical

Property	Value	Condition	Related Standards	Comment
Bending Fatigue Strength	135.0 MPa	H14	EN 573-3, EN 1592, EN 485, EN 754
Elastic modulus	71.0 GPa	H14	EN 573-3, EN 1592, EN 485, EN 754
Hardness, Brinell	90.0 [-]	H14	EN 573-3, EN 485
Plane-Strain Fracture Toughnes	22.0 - 35.0 MPa·√m			Typical for Wrought 5000 Series Aluminium
Poisson's ratio	0.33 [-]			Typical for Wrought 5000 Series Aluminium
Shear modulus	26.7 GPa	H14	EN 573-3, EN 1592, EN 485, EN 754
Tensile strength	295.0 MPa	H14	EN 573-3, EN 754
	300.0 MPa	H14	EN 573-3, EN 1592
	300.0 - 360.0 MPa	H14	EN 573-3, EN 485

Thermal

Property	Temperature	Value	Condition	Related Standards	Comment
Coefficient of thermal expansion	-50 °C	2.2e-05 1/K	H14	EN 573-3, EN 1592, EN 485, EN 754
	20 °C	2.2e-05 1/K	H14	EN 573-3, EN 1592, EN 485, EN 754
	20 °C	2.38e-05 1/K	H14	EN 573-3, EN 1592, EN 485, EN 754
	20 °C	2.4699999999999997e-05 1/K	H14	EN 573-3, EN 1592, EN 485, EN 754
	20 °C	2.58e-05 1/K	H14	EN 573-3, EN 1592, EN 485, EN 754
	100 °C	2.38e-05 1/K	H14	EN 573-3, EN 1592, EN 485, EN 754
	200 °C	2.4699999999999997e-05 1/K	H14	EN 573-3, EN 1592, EN 485, EN 754
	300 °C	2.58e-05 1/K	H14	EN 573-3, EN 1592, EN 485, EN 754
Max service temperature		150.0 °C			Typical for Wrought 5000 Series Aluminium
Melting point		585.0 - 641.0 °C	H14	EN 573-3, EN 1592, EN 485, EN 754
		585.0 - 640.0 °C	H14	EN 573-3, EN 1592, EN 485, EN 754
Specific heat capacity		900.0 J/(kg·K)	H14	EN 573-3, EN 1592, EN 485, EN 754
Thermal conductivity		120.0 - 140.0 W/(m·K)	H14	EN 573-3, EN 1592, EN 485, EN 754
		126 W/(m·K)	H14	EN 573-3, EN 1592, EN 485, EN 754

Electrical

Property	Value	Condition	Related Standards
Electrical conductivity	17000000.0 - 19000000.0 S/m	H14	EN 573-3, EN 1592, EN 485, EN 754
	18000000.0 S/m	H14	EN 573-3, EN 1592, EN 485, EN 754
Electrical resistivity	5.26e-08 - 5.88e-08 Ω·m	H14	EN 573-3, EN 1592, EN 485, EN 754
	5.56e-08 Ω·m	H14	EN 573-3, EN 1592, EN 485, EN 754

Chemical properties

Property	Value	Condition	Related Standards
Chromium	0.05 - 0.25 %	H14	EN 573-3, EN 1592, EN 485, EN 754
Copper	0.1 %	H14	EN 573-3, EN 1592, EN 485, EN 754
Iron	0.50 %	H14	EN 573-3, EN 1592, EN 485, EN 754
Magnesium	3.5 - 4.5 %	H14	EN 573-3, EN 1592, EN 485, EN 754
Manganese	0.2 - 0.7 %	H14	EN 573-3, EN 1592, EN 485, EN 754
Silicon	0.4 %	H14	EN 573-3, EN 1592, EN 485, EN 754
Titanium	0.15 %	H14	EN 573-3, EN 1592, EN 485, EN 754
Zinc	0.25 %	H14	EN 573-3, EN 1592, EN 485, EN 754

Technological properties

Property
Anodizing	decorative: acceptable, Protective: very good
Brazing	hard brazing (with flux/ without flux): poor / sufficient, friction soldering: acceptable, soft brazing with flux: poor
Workability	Bending / Spinning (cold): good / sufficient, Impact extrusion (cold): sufficient, Deep drawing / upsetting (Condition) good (O) / good (O)

Property

Anodizing

decorative: acceptable, Protective: very good

Brazing

hard brazing (with flux/ without flux): poor / sufficient, friction soldering: acceptable, soft brazing with flux: poor

Workability

Bending / Spinning (cold): good / sufficient, Impact extrusion (cold): sufficient, Deep drawing / upsetting (Condition) good (O) / good (O)

DIN 1725-1 Grade 3.3316 H24 Aluminium-Magnesium Alloy – Superior Corrosion Resistance & Machinability DIN 1725-1 Grade 3.4345 T6 Aluminum Alloy – High Strength & Corrosion Resistance