EN 573-3 Grade 3.0517 F Aluminum Alloy – Superior Corrosion Resistance & Versatile Fabrication

Aluminum DIN 3.0517 is a popular alloy that offers customers very good atmospheric corrosion resistance and moderate strength. Aluminum 3003 offers good machinability for aluminum alloys, though it is not heat treatable. Unlike other aluminum alloys, DIN 3.0517 is weldable by conventional welding methods. It also takes cold and hot working well and has generally better mechanical properties when compared to 1000 series aluminum alloys.

Properties

General

Property	Value	Condition	Related Standards
Density	2.73 g/cm³	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 570, EN 755

Mechanical

Property	Value	Condition	Related Standards	Comment
Elastic modulus	69.0 GPa	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 570, EN 755
	69.5 GPa	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 570, EN 755
Hardness, Brinell	33.0 [-]	F	EN 573-3, EN 570
Plane-Strain Fracture Toughnes	22.0 - 35.0 MPa·√m			Typical for Wrought 3000 Series Aluminium
Poisson's ratio	0.33 [-]			Typical for Wrought 3000 Series Aluminium
Shear modulus	26.1 GPa	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 570, EN 755
Tensile strength	95.0 MPa	F	EN 573-3, EN 485, EN 755
	120.0 - 220.0 MPa	F	EN 573-3, EN 1715-3

Thermal

Property	Temperature	Value	Condition	Related Standards
Coefficient of thermal expansion	-50 °C	2.1499999999999997e-05 1/K	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 570, EN 755
	20 °C	2.1499999999999997e-05 1/K	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 570, EN 755
	20 °C	2.3199999999999998e-05 1/K	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 570, EN 755
	20 °C	2.41e-05 1/K	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 570, EN 755
	20 °C	2.52e-05 1/K	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 570, EN 755
	100 °C	2.3199999999999998e-05 1/K	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 570, EN 755
	200 °C	2.41e-05 1/K	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 570, EN 755
	300 °C	2.52e-05 1/K	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 570, EN 755
Melting point		640.0 - 655.0 °C	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 570, EN 755
		643.0 - 654.0 °C	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 570, EN 755
Specific heat capacity		893.0 J/(kg·K)	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 570, EN 755
Thermal conductivity		159.0 - 193.0 W/(m·K)	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 570, EN 755
		160.0 - 200.0 W/(m·K)	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 570, EN 755

Electrical

Property	Value	Condition	Related Standards
Electrical conductivity	23000000.0 - 29000000.0 S/m	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 570, EN 755
	24000000.0 - 29000000.0 S/m	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 570, EN 755
Electrical resistivity	3.45e-08 - 4.17e-08 Ω·m	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 570, EN 755
	3.45e-08 - 4.35e-08 Ω·m	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 570, EN 755

Chemical properties

Property	Value	Condition	Related Standards
Copper	0.05 - 0.2 %	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 570, EN 755
Iron	0.70 %	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 570, EN 755
Manganese	1.0 - 1.5 %	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 570, EN 755
Silicon	0.6 %	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 570, EN 755
Zinc	0.1 %	F	EN 573-3, EN 1386, EN 1715-3, EN 485, EN 570, EN 755

Technological properties

Property
Anodizing	decorative: sufficient, Protective: very good
Brazing	hard brazing (with flux/ without flux): very good / very good, friction soldering: very good, soft brazing with flux: very good
Corrosion properties	Seawater: good, weathering: very good
Workability	Bending / Spinning (cold): very good / very good, Impact extrusion (cold): acceptable, Deep drawing / upsetting (Condition) very good (O) / very good (H12)