EN 573-3: Grade 3.0517 H111 – Durable, Corrosion‑Resistant Aluminum Alloy

Aluminum DIN 3.0517 is a popular alloy that offers customers very good atmospheric corrosion resistance and moderate strength. Aluminum 3003 offers good machinability for aluminum alloys, though it is not heat treatable. Unlike other aluminum alloys, DIN 3.0517 is weldable by conventional welding methods. It also takes cold and hot working well and has generally better mechanical properties when compared to 1000 series aluminum alloys.

Properties

General

Property	Value	Condition	Related Standards
Density	2.73 g/cm³	H111	EN 573-3, EN 485, EN 754, EN 755

Mechanical

Property	Value	Condition	Related Standards	Comment
Bending angle 180°	1.0 °/t	H111	EN 573-3, EN 485
Bending angle 90°	1.0 °/t	H111	EN 573-3, EN 485
	1.5 °/t	H111	EN 573-3, EN 485
Elastic modulus	69.0 GPa	H111	EN 573-3, EN 485, EN 754, EN 755
	69.5 GPa	H111	EN 573-3, EN 485, EN 754, EN 755
Hardness, Brinell	28.0 [-]	H111	EN 573-3, EN 485
Plane-Strain Fracture Toughnes	22.0 - 35.0 MPa·√m			Typical for Wrought 3000 Series Aluminium
Poisson's ratio	0.33 [-]			Typical for Wrought 3000 Series Aluminium
Shear modulus	26.1 GPa	H111	EN 573-3, EN 485, EN 754, EN 755
Tensile strength	95.0 - 135.0 MPa	H111	EN 573-3, EN 485, EN 755
	95.0 - 130.0 MPa	H111	EN 573-3, EN 754

Thermal

Property	Temperature	Value	Condition	Related Standards
Coefficient of thermal expansion	-50 °C	2.1499999999999997e-05 1/K	H111	EN 573-3, EN 485, EN 754, EN 755
	20 °C	2.1499999999999997e-05 1/K	H111	EN 573-3, EN 485, EN 754, EN 755
	20 °C	2.3199999999999998e-05 1/K	H111	EN 573-3, EN 485, EN 754, EN 755
	20 °C	2.41e-05 1/K	H111	EN 573-3, EN 485, EN 754, EN 755
	20 °C	2.52e-05 1/K	H111	EN 573-3, EN 485, EN 754, EN 755
	100 °C	2.3199999999999998e-05 1/K	H111	EN 573-3, EN 485, EN 754, EN 755
	200 °C	2.41e-05 1/K	H111	EN 573-3, EN 485, EN 754, EN 755
	300 °C	2.52e-05 1/K	H111	EN 573-3, EN 485, EN 754, EN 755
Melting point		640.0 - 655.0 °C	H111	EN 573-3, EN 485, EN 754, EN 755
		643.0 - 654.0 °C	H111	EN 573-3, EN 485, EN 754, EN 755
Specific heat capacity		893.0 J/(kg·K)	H111	EN 573-3, EN 485, EN 754, EN 755
Thermal conductivity		159.0 - 193.0 W/(m·K)	H111	EN 573-3, EN 485, EN 754, EN 755
		160.0 - 200.0 W/(m·K)	H111	EN 573-3, EN 485, EN 754, EN 755

Electrical

Property	Value	Condition	Related Standards
Electrical conductivity	23000000.0 - 29000000.0 S/m	H111	EN 573-3, EN 485, EN 754, EN 755
	24000000.0 - 29000000.0 S/m	H111	EN 573-3, EN 485, EN 754, EN 755
Electrical resistivity	3.45e-08 - 4.17e-08 Ω·m	H111	EN 573-3, EN 485, EN 754, EN 755
	3.45e-08 - 4.35e-08 Ω·m	H111	EN 573-3, EN 485, EN 754, EN 755

Chemical properties

Property	Value	Condition	Related Standards
Copper	0.05 - 0.2 %	H111	EN 573-3, EN 485, EN 754, EN 755
Iron	0.70 %	H111	EN 573-3, EN 485, EN 754, EN 755
Manganese	1.0 - 1.5 %	H111	EN 573-3, EN 485, EN 754, EN 755
Silicon	0.6 %	H111	EN 573-3, EN 485, EN 754, EN 755
Zinc	0.1 %	H111	EN 573-3, EN 485, EN 754, EN 755

Technological properties

Property
Anodizing	decorative: sufficient, Protective: very good
Brazing	hard brazing (with flux/ without flux): very good / very good, friction soldering: very good, soft brazing with flux: very good
Corrosion properties	Seawater: good, weathering: very good
Workability	Bending / Spinning (cold): very good / very good, Impact extrusion (cold): acceptable, Deep drawing / upsetting (Condition) very good (O) / very good (H12)