EN 573-3 AW-6063 H111 Aluminum Alloy – Superior Corrosion Resistance & Finish
Aluminum EN AW-6063 is an architectural alloy that offers users a high resistance to corrosion and excellent finishing characteristics. Easy to extrude with fair machinability, EN AW-6063 can be both hot and cold formed and is commonly available as T6 temper as well as T4 temper.
Properties
General
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Density | 2.7 g/cm³ | H111 | EN 573-3, EN 754, EN 755 | Strip, Sheet, Plate, Tube, Bar |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Elastic modulus | 69.0 GPa | H111 | EN 573-3, EN 754, EN 755 | Strip, Sheet, Plate, Tube, Bar | ||
69.5 GPa | H111 | EN 573-3, EN 754, EN 755 | Strip, Sheet, Plate, Tube, Bar | |||
Elongation | 15.0 % | H111 | EN 573-3, EN 754 | Strip, Sheet, Plate, Tube, Bar | A50 | |
16.0 % | H111 | EN 573-3, EN 755 | Strip, Sheet, Plate, Tube, Bar | A50 | ||
18.0 % | H111 | EN 573-3, EN 755 | Strip, Sheet, Plate, Tube, Bar | A100 | ||
20.0 % | H111 | EN 573-3, EN 754 | Strip, Sheet, Plate, Tube, Bar | A100 | ||
20.0 °C | 13.0 % | H111 | EN 573-3 | Rod, Tube | A50 | |
20.0 °C | 14.0 % | H111 | EN 573-3 | Rod, Tube | A50 | |
20.0 °C | 15.0 % | H111 | EN 573-3 | Tube | A50 | |
20.0 °C | 15.0 % | H111 | EN 573-3 | Rod, Tube | ||
20.0 °C | 16.0 % | H111 | EN 573-3 | Rod, Tube | A50 | |
20.0 °C | 16.0 % | H111 | EN 573-3 | Rod, Tube | ||
20.0 °C | 18.0 % | H111 | EN 573-3 | Rod, Tube | ||
20.0 °C | 20.0 % | H111 | EN 573-3 | Tube | ||
Hardness, Brinell | 20.0 °C | 25.0 [-] | H111 | EN 573-3 | Rod, Tube | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 6000 Series Aluminium | ||||
Poisson's ratio | 0.33 [-] | Typical for Wrought 6000 Series Aluminium | ||||
Shear modulus | 26.1 GPa | H111 | EN 573-3, EN 754, EN 755 | Strip, Sheet, Plate, Tube, Bar | ||
Tensile strength | 130.0 | H111 | EN 573-3, EN 755 | Strip, Sheet, Plate, Tube, Bar | ||
155.0 | H111 | EN 573-3, EN 754 | Strip, Sheet, Plate, Tube, Bar | |||
20.0 °C | 130.0 | H111 | EN 573-3 | Rod, Tube | ||
20.0 °C | 140.0 | H111 | EN 573-3 | Rod, Tube | ||
20.0 °C | 150.0 | H111 | EN 573-3 | Rod, Tube | ||
20.0 °C | 155.0 | H111 | EN 573-3 | Tube |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.3399999999999996e-05 1/K | H111 | EN 573-3, EN 754, EN 755 | Strip, Sheet, Plate, Tube, Bar | |
100 °C | 2.3399999999999996e-05 1/K | H111 | EN 573-3, EN 754, EN 755 | Strip, Sheet, Plate, Tube, Bar | ||
Melting point | 615.0 - 655.0 °C | H111 | EN 573-3, EN 754, EN 755 | Strip, Sheet, Plate, Tube, Bar | ||
Specific heat capacity | 887.0 - 963.0 J/(kg·K) | Typical for Wrought 6000 Series Aluminium | ||||
Thermal conductivity | 193.0 - 218.0 W/(m·K) | H111 | EN 573-3, EN 754, EN 755 | Strip, Sheet, Plate, Tube, Bar |
Electrical
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Electrical conductivity | 29000000.0 - 34000000.0 S/m | H111 | EN 573-3, EN 754, EN 755 | Strip, Sheet, Plate, Tube, Bar |
Electrical resistivity | 2.94e-08 - 3.45e-08 Ω·m | H111 | EN 573-3, EN 754, EN 755 | Strip, Sheet, Plate, Tube, Bar |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Chromium | 0.05 % | H111 | EN 573-3 | Rod, Tube |
0.1 % | H111 | EN 573-3, EN 754, EN 755 | Rod, Tube, Strip, Sheet, Plate, Bar | |
Copper | 0.1 % | H111 | EN 573-3, EN 754, EN 755 | Rod, Tube, Strip, Sheet, Plate, Bar |
Iron | 0.15 - 0.35 % | H111 | EN 573-3 | Rod, Tube |
0.35 % | H111 | EN 573-3 | Rod, Tube | |
0.35 % | H111 | EN 573-3, EN 754, EN 755 | Strip, Sheet, Plate, Tube, Bar | |
Magnesium | 0.45 - 0.9 % | H111 | EN 573-3, EN 754, EN 755 | Rod, Tube, Strip, Sheet, Plate, Bar |
0.6 - 0.9 % | H111 | EN 573-3 | Rod, Tube | |
Manganese | 0.1 % | H111 | EN 573-3, EN 754, EN 755 | Rod, Tube, Strip, Sheet, Plate, Bar |
0.15 % | H111 | EN 573-3 | Rod, Tube | |
Silicon | 0.2 - 0.6 % | H111 | EN 573-3, EN 754, EN 755 | Rod, Tube, Strip, Sheet, Plate, Bar |
0.3 - 0.6 % | H111 | EN 573-3 | Rod, Tube | |
Titanium | 0.1 % | H111 | EN 573-3, EN 754, EN 755 | Rod, Tube, Strip, Sheet, Plate, Bar |
Zinc | 0.1 % | H111 | EN 573-3, EN 754, EN 755 | Rod, Tube, Strip, Sheet, Plate, Bar |
0.15 % | H111 | EN 573-3 | Rod, Tube |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | decorative: acceptable, Protective: very good | |
| Brazing | hard brazing (with flux/ without flux): acceptable to poor / sufficient, friction soldering: good, soft brazing with flux: acceptable | |
| Corrosion properties | Seawater: good to acceptable, weathering: good | |
| Workability | Excellent workability. | |
Metal
- EN 573-3 Grade 3.0915 (H111) – Premium Aluminium Alloy
- EN 573-3 Grade 3.3326 H111 – Detailed Mechanical Properties of 5000 Series Aluminium
- EN 573-3 Grade 3.0505 H111 Aluminium Alloy - Technical Specifications
- AW‑5186 H111 Aluminium Alloy – EN 573‑3 Certified for High‑Performance Applications
- EN 573-3 Grade 3.0257 H111 Aluminium Alloy Specifications
- EN 573-3 Grade 3.3549 H111 Aluminium Alloy – Technical Specifications and R&D Services
- EN 573-3 Grade 3.1325 H111 – Aluminium Alloy Properties & Standards
- EN 573-3 Grade 3.2315 H111 – Detailed Aluminium Alloy Specifications
- EN 573-3 Grade 3.0515 H111 Steel – Comprehensive Properties & Compliance
- EN AW-6063 (Grade F) – High-Performance Architectural Aluminum Alloy