Aluminum 5657 H22 Non-Heat Treatable Wrought Alloy – Superior Finish & Corrosion Resistance
Excellent surface finishing properties (bright, anodizing...) and corrosion resistance.
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 23.0 °C | 2.69 g/cm³ |
Dimension
| Property | Value |
|---|---|
Thickness | 0.3 - 1.2 mm |
Mechanical
| Property | Temperature | Value |
|---|---|---|
Elastic modulus | 23.0 °C | 70 GPa |
Elongation A50 | 23.0 °C | 10 % |
Shear modulus | 23.0 °C | 26.5 GPa |
Tensile strength | 23.0 °C | 120 - 160 MPa |
Yield strength | 23.0 °C | 80 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 100.0 °C | 2.4E-5 1/K | 20-100°C |
Thermal conductivity | 23.0 °C | 138 W/(m·K) |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical resistivity | 23.0 °C | 4.9E-8 Ω·m |
Chemical properties
| Property | Value |
|---|---|
Copper | 0.1 % |
Iron | 0.1 % |
Magnesium | 0.6 - 1 % |
Manganese | 0.03 % |
Other | 0.05 % |
Silicon | 0.08 % |
Zinc | 0.05 % |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | Excellent | |
| Application areas | Interiors and ceilings: Single sheet, Sheets for composites/ sandwich Panels; Anodizing quality; Cosmetics: Cosmetics pieces; Automotive trim: Interior trim, Window frame, Marque badges | |
| Corrosion properties | Excellent | |
| General machinability | Good | |
| Welding | Good | |
| Workability | Good | |
Metal
- 5252-O: High-Purity, Non-Heat-Treatable Aluminum Wrought Alloy for Superior Brightening and Anodizing
- 1350 H19 Non-Heat-Treatable Al Wrought Alloy – High Conductivity & Mechanical Strength
- 1350 H22 Non-Heat-Treatable Aluminum Wrought Alloy – Superior Conductivity & Performance
- 8011A O – Non‑Heat Treatable Aluminum Wrought Alloy: Key Properties & Applications
- 1200 H22 Non-Heat-Treatable Aluminum Wrought Alloy – Superior Corrosion Resistance & Workability
- Aluminum 5657 H242 Non-Heat Treatable Wrought Alloy – Superior Corrosion Resistance & Surface Finish
- Aluminum Alloy 5657 H28 – Non-Heat Treatable, Superior Surface Finish & Corrosion Resistance
- 5251 O: High-Strength, Formable Non-Heat-Treatable Aluminum Wrought Alloy
- 5251 H22 Non-Heat Treated Aluminium Wrought Alloy – Medium Strength, Excellent Formability & Corrosion Resistance
- 3103-O: High-Strength, Non-Heat-Treatable Aluminum Alloy for Structural Applications