High-Strength Aluminum-Nickel-Bronze TQ50 Tube (C95510) – Superior Durability & Machinability

Materion Performance Alloy C95510 is an Aluminum-Nickel-Bronze alloys that combine high strength, ductility, and good abrasion resistance under severe loading conditions. Materion uses the EquaCast® process to produce C95510. This process produces an extremely uniform, fine grained microstructure and excellent dispersion of alloying elements, providing improved product consistency, quality and machinability.

Properties

General

Property	Temperature	Value
Density	23.0 °C	7.5 g/cm³

Dimension

Property	Value	Comment
Outside diameter	406 mm	max.
Length	contact the supplier
Wall thickness	Nominally 10-20% of OD

Mechanical

Property	Temperature	Value
Elastic modulus	23.0 °C	110 GPa
Elongation	23.0 °C	9 %
Tensile strength	23.0 °C	655 - 724 MPa
Yield strength Rp0.2	23.0 °C	386 - 431 MPa

Thermal

Property	Temperature	Value
Coefficient of thermal expansion	23.0 °C	1.6E-5 1/K
Melting point		1040 °C
Thermal conductivity	23.0 °C	42 W/(m·K)

Electrical

Property	Temperature	Value
Electrical resistivity	23.0 °C	2E-7 Ω·m
Specific Electrical conductivity		8 % IACS

Magnetic

Property	Temperature	Value
Relative magnetic permeability	23.0 °C	1.1 - 1.2 [-]

Chemical properties

Property	Value	Comment
Aluminium	9.7 - 10.9 %
Copper	78 %
Iron	2 - 3.5 %
Manganese	1.5 %	max.
Nickel	4.5 - 5.5 %
Tin	0.2 %	max.
Zinc	0.3 %	max.

Technological properties

Property
Application areas	Aerospace applications, including, but not limited to: bushings, spherical and rod end bearings, rub pads, and wear strips. They are also commonly used for applications in the oil & gas and other durable goods markets.