EN 573-3 Grade AW-2007 T3510 – High-Strength Age-Hardenable AlCu Alloy

Age-hardenable AlCu alloy. The alloy is not food safe.

Additional services: Cuttings, Parts from drawings

Properties

General

Property	Temperature	Value	Condition	Related Standards	Shape
Density		2.85 g/cm³	T3510	EN 573-3, EN 754	Rod, Tube
	20.0 °C	2.85 g/cm³	T3510	EN 573-3	Tube

Mechanical

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Elastic modulus		72.5 GPa	T3510	EN 573-3, EN 754	Rod, Tube
Elongation		3.0 %	T3510	EN 573-3, EN 754	Rod, Tube	A50
		5.0 %	T3510	EN 573-3, EN 754	Rod, Tube	A100
	20.0 °C	3.0 %	T3510	EN 573-3	Tube	A50
	20.0 °C	5.0 %	T3510	EN 573-3	Tube
Hardness, Brinell	20.0 °C	95.0 [-]	T3510	EN 573-3	Tube
Plane-Strain Fracture Toughnes		22.0 - 35.0 MPa·√m				Typical for Wrought 2000 Series Aluminium
Poisson's ratio		0.33 [-]				Typical for Wrought 2000 Series Aluminium
Shear modulus		27.3 GPa	T3510	EN 573-3, EN 754	Rod, Tube
Tensile strength		370.0 MPa	T3510	EN 573-3, EN 754	Rod, Tube
	20.0 °C	370.0 MPa	T3510	EN 573-3	Tube

Thermal

Property	Temperature	Value	Condition	Related Standards	Shape
Coefficient of thermal expansion	20 °C	2.3e-05 1/K	T3510	EN 573-3, EN 754	Rod, Tube
	100 °C	2.3e-05 1/K	T3510	EN 573-3, EN 754	Rod, Tube
	100.0 °C	2.4e-05 1/K	T3510	EN 573-3	Tube
Melting point		507.0 - 650.0 °C	T3510	EN 573-3, EN 754	Rod, Tube
Specific heat capacity		860.0 J/(kg·K)	T3510	EN 573-3, EN 754	Rod, Tube
	20.0 °C	860.0 J/(kg·K)	T3510	EN 573-3	Tube
Thermal conductivity		130.0 - 160.0 W/(m·K)	T3510	EN 573-3, EN 754	Rod, Tube
	20.0 °C	116.0 - 168.0 W/(m·K)	T3510	EN 573-3	Tube

Electrical

Property	Temperature	Value	Condition	Related Standards	Shape
Electrical conductivity	20.0 °C	18000000.0 - 22000000.0 S/m	T3510	EN 573-3, EN 754	Tube, Rod
Electrical resistivity		4.55e-08 - 5.56e-08 Ω·m	T3510	EN 573-3, EN 754	Rod, Tube

Chemical properties

Property	Value	Condition	Related Standards	Shape
Bismuth	0.2 %	T3510	EN 573-3, EN 754	Tube, Rod
Chromium	0.1 %	T3510	EN 573-3, EN 754	Tube, Rod
Copper	3.3 - 4.6 %	T3510	EN 573-3, EN 754	Tube, Rod
Iron	0.8 %	T3510	EN 573-3	Tube
	0.80 %	T3510	EN 573-3, EN 754	Rod, Tube
Lead	0.8 - 1.5 %	T3510	EN 573-3, EN 754	Tube, Rod
Magnesium	0.4 - 1.8 %	T3510	EN 573-3, EN 754	Tube, Rod
Manganese	0.5 - 1.0 %	T3510	EN 573-3, EN 754	Tube, Rod
Nickel	0.2 %	T3510	EN 573-3, EN 754	Tube, Rod
Silicon	0.8 %	T3510	EN 573-3, EN 754	Tube, Rod
Tin	0.2 %	T3510	EN 573-3, EN 754	Tube, Rod
Titanium	0.2 %	T3510	EN 573-3, EN 754	Tube, Rod
Zinc	0.8 %	T3510	EN 573-3, EN 754	Tube, Rod

Technological properties

Property
Anodizing	Protective: poor
Brazing	friction soldering: sufficient
Corrosion properties	Seawater: poor, weathering: poor
Workability	Bending / Spinning (cold): sufficient / -, Deep drawing / upsetting (Condition) - / sufficient