EN 573-3 Grade AW-2007 T4511 – High-Strength Age-Hardenable AlCu Alloy
Age-hardenable AlCu alloy. The alloy is not food safe.
Additional services: Cuttings, Parts from drawingsProperties
General
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Density | 2.85 g/cm³ | T4511 | EN 573-3, EN 755 | Rod, Tube | |
20.0 °C | 2.85 g/cm³ | T4511 | EN 573-3 | Profile, Rod, Tube |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
|---|---|---|---|---|---|---|
Elastic modulus | 72.5 GPa | T4511 | EN 573-3, EN 755 | Rod, Tube | ||
Elongation | 6.0 % | T4511 | EN 573-3, EN 755 | Rod, Tube | A50 | |
7.0 % | T4511 | EN 573-3, EN 755 | Rod, Tube | A100 | ||
8.0 % | T4511 | EN 573-3, EN 755 | Rod, Tube | A100 | ||
20.0 °C | 6.0 % | T4511 | EN 573-3 | Profile, Rod, Tube | A50 | |
20.0 °C | 7.0 % | T4511 | EN 573-3 | Rod | ||
20.0 °C | 8.0 % | T4511 | EN 573-3 | Profile, Tube, Rod | ||
Hardness, Brinell | 20.0 °C | 95.0 [-] | T4511 | EN 573-3 | Profile, Rod, Tube | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | ||||
Poisson's ratio | 0.33 [-] | Typical for Wrought 2000 Series Aluminium | ||||
Shear modulus | 27.3 GPa | T4511 | EN 573-3, EN 755 | Rod, Tube | ||
Tensile strength | 330.0 MPa | T4511 | EN 573-3, EN 755 | Rod, Tube | ||
340.0 MPa | T4511 | EN 573-3, EN 755 | Rod, Tube | |||
370.0 MPa | T4511 | EN 573-3, EN 755 | Rod, Tube | |||
20.0 °C | 330.0 MPa | T4511 | EN 573-3 | Rod | ||
20.0 °C | 340.0 MPa | T4511 | EN 573-3 | Rod | ||
20.0 °C | 370.0 MPa | T4511 | EN 573-3 | Profile, Tube, Rod |
Thermal
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.3e-05 1/K | T4511 | EN 573-3, EN 755 | Rod, Tube |
100 °C | 2.3e-05 1/K | T4511 | EN 573-3, EN 755 | Rod, Tube | |
100.0 °C | 2.4e-05 1/K | T4511 | EN 573-3 | Profile, Rod, Tube | |
Melting point | 507.0 - 650.0 °C | T4511 | EN 573-3, EN 755 | Rod, Tube | |
Specific heat capacity | 860.0 J/(kg·K) | T4511 | EN 573-3, EN 755 | Rod, Tube | |
20.0 °C | 860.0 J/(kg·K) | T4511 | EN 573-3 | Profile, Rod, Tube | |
Thermal conductivity | 130.0 - 160.0 W/(m·K) | T4511 | EN 573-3, EN 755 | Rod, Tube | |
20.0 °C | 116.0 - 168.0 W/(m·K) | T4511 | EN 573-3 | Profile, Rod, Tube |
Electrical
| Property | Temperature | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|---|
Electrical conductivity | 20.0 °C | 18000000.0 - 22000000.0 S/m | T4511 | EN 573-3, EN 755 | Profile, Rod, Tube |
Electrical resistivity | 4.55e-08 - 5.56e-08 Ω·m | T4511 | EN 573-3, EN 755 | Rod, Tube |
Chemical properties
| Property | Value | Condition | Related Standards | Shape |
|---|---|---|---|---|
Bismuth | 0.2 % | T4511 | EN 573-3, EN 755 | Profile, Rod, Tube |
Chromium | 0.1 % | T4511 | EN 573-3, EN 755 | Profile, Rod, Tube |
Copper | 3.3 - 4.6 % | T4511 | EN 573-3, EN 755 | Profile, Rod, Tube |
Iron | 0.8 % | T4511 | EN 573-3 | Profile, Rod, Tube |
0.80 % | T4511 | EN 573-3, EN 755 | Rod, Tube | |
Lead | 0.8 - 1.5 % | T4511 | EN 573-3, EN 755 | Profile, Rod, Tube |
Magnesium | 0.4 - 1.8 % | T4511 | EN 573-3, EN 755 | Profile, Rod, Tube |
Manganese | 0.5 - 1.0 % | T4511 | EN 573-3, EN 755 | Profile, Rod, Tube |
Nickel | 0.2 % | T4511 | EN 573-3, EN 755 | Profile, Rod, Tube |
Silicon | 0.8 % | T4511 | EN 573-3, EN 755 | Profile, Rod, Tube |
Tin | 0.2 % | T4511 | EN 573-3, EN 755 | Profile, Rod, Tube |
Titanium | 0.2 % | T4511 | EN 573-3, EN 755 | Profile, Rod, Tube |
Zinc | 0.8 % | T4511 | EN 573-3, EN 755 | Profile, Rod, Tube |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | Protective: poor | |
| Brazing | friction soldering: sufficient | |
| Corrosion properties | Seawater: poor, weathering: poor | |
| Workability | Bending / Spinning (cold): sufficient / -, Deep drawing / upsetting (Condition) - / sufficient | |
Metal
- AW-8014 O – Food-Safe, High-Performance Aluminum Alloy (EN 573-3)
- AW-8111 O Aluminium Alloy – EN 573‑3 Grade, Food Safe & High Strength
- EN 573-3 Grade AW-2091: Premium Age-Hardenable AlCu Alloy for Structural Applications
- EN 573-3 AW-2007 T3511 Aluminum Alloy – High-Strength, Age-Hardenable Grade
- EN 573-3 AW-2007 T4 – High‑Strength Age‑Hardenable Aluminum Alloy
- EN 573-3 Grade AW-2007 T3510 – High-Strength Age-Hardenable AlCu Alloy
- AW-2007 T4510 Aluminum Alloy – EN 573-3 Grade
- EN 573-3 Grade AW-2014 T4511 Aluminum Alloy – Superior Strength & Machinability
- AW-2007 T3: EN 573-3 Grade Aluminum Alloy – Specifications & Properties
- AW-2007 T351 Aluminum Alloy – EN 573-3 Grade for Engineering Applications