EN 573-3 Grade AW-2014 T3511 – High-Performance Aluminum Alloy

EN AW-2014 is an alloy with strength, machinability and welding capabilities, Aluminum Alloy EN AW-2014 is an excellent option. It is a precipitation hardening alloy that maintains strength after heat treatment.

Properties

General

Property	Temperature	Value	Condition	Related Standards	Shape
Density		2.8 g/cm³	T3511	EN 573-3, EN 754	Strip, Sheet, Plate, Forging, Tube, Bar
	20.0 °C	2.8 g/cm³	T3511	EN 573-3	Tube

Mechanical

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Elastic modulus		73.0 GPa	T3511	EN 573-3, EN 754	Strip, Sheet, Plate, Forging, Tube, Bar
	20.0 °C	72.0 GPa	T3511	EN 573-3	Tube
Elongation		4.0 %	T3511	EN 573-3, EN 754	Strip, Sheet, Plate, Forging, Tube, Bar	A50
		6.0 %	T3511	EN 573-3, EN 754	Strip, Sheet, Plate, Forging, Tube, Bar	A100
	20.0 °C	4.0 %	T3511	EN 573-3	Tube	A50
	20.0 °C	6.0 %	T3511	EN 573-3	Tube
Hardness, Brinell	20.0 °C	110.0 [-]	T3511	EN 573-3	Tube
Plane-Strain Fracture Toughnes		22.0 - 35.0 MPa·√m				Typical for Wrought 2000 Series Aluminium
Poisson's ratio		0.33 [-]				Typical for Wrought 2000 Series Aluminium
Shear modulus		27.4 GPa	T3511	EN 573-3, EN 754	Strip, Sheet, Plate, Forging, Tube, Bar
Tensile strength		380.0 MPa	T3511	EN 573-3, EN 754	Strip, Sheet, Plate, Forging, Tube, Bar
	20.0 °C	380.0 MPa	T3511	EN 573-3	Tube

Thermal

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Coefficient of thermal expansion	-50 °C	2.1e-05 1/K	T3511	EN 573-3, EN 754	Strip, Sheet, Plate, Forging, Tube, Bar
	-50.0 °C	2.1e-05 1/K	T3511	EN 573-3, EN 754	Strip, Sheet, Plate, Forging, Tube, Bar
	20 °C	2.1e-05 1/K	T3511	EN 573-3, EN 754	Strip, Sheet, Plate, Forging, Tube, Bar
	20 °C	2.28e-05 1/K	T3511	EN 573-3, EN 754	Strip, Sheet, Plate, Forging, Tube, Bar
	20 °C	2.3e-05 1/K	T3511	EN 573-3, EN 754	Strip, Sheet, Plate, Forging, Tube, Bar
	20 °C	2.36e-05 1/K	T3511	EN 573-3, EN 754	Strip, Sheet, Plate, Forging, Tube, Bar
	20 °C	2.46e-05 1/K	T3511	EN 573-3, EN 754	Strip, Sheet, Plate, Forging, Tube, Bar
	100 °C	2.28e-05 1/K	T3511	EN 573-3, EN 754	Strip, Sheet, Plate, Forging, Tube, Bar
	100.0 °C	2.28e-05 1/K	T3511	EN 573-3, EN 754	Strip, Sheet, Plate, Forging, Tube, Bar
	100 °C	2.3e-05 1/K	T3511	EN 573-3, EN 754	Strip, Sheet, Plate, Forging, Tube, Bar
	200 °C	2.36e-05 1/K	T3511	EN 573-3, EN 754	Strip, Sheet, Plate, Forging, Tube, Bar
	200.0 °C	2.36e-05 1/K	T3511	EN 573-3, EN 754	Strip, Sheet, Plate, Forging, Tube, Bar
	300 °C	2.46e-05 1/K	T3511	EN 573-3, EN 754	Strip, Sheet, Plate, Forging, Tube, Bar
	300.0 °C	2.46e-05 1/K	T3511	EN 573-3, EN 754	Strip, Sheet, Plate, Forging, Tube, Bar
Melting point		505.0 - 635.0 °C	T3511	EN 573-3, EN 754	Strip, Sheet, Plate, Forging, Tube, Bar
		510.0 - 640.0 °C	T3511	EN 573-3, EN 754	Strip, Sheet, Plate, Forging, Tube, Bar
Specific heat capacity		816.0 - 963.0 J/(kg·K)				Typical for Wrought 2000 Series Aluminium
Thermal conductivity		134.0 - 193.0 W/(m·K)	T3511	EN 573-3, EN 754	Strip, Sheet, Plate, Forging, Tube, Bar
	20.0 °C	140.0 - 200.0 W/(m·K)	T3511	EN 573-3, EN 754	Tube, Strip, Sheet, Plate, Forging, Bar

Electrical

Property	Temperature	Value	Condition	Related Standards	Shape
Electrical conductivity		21000000.0 - 24000000.0 S/m	T3511	EN 573-3, EN 754	Strip, Sheet, Plate, Forging, Tube, Bar
	20.0 °C	20000000.0 - 29000000.0 S/m	T3511	EN 573-3, EN 754	Tube, Strip, Sheet, Plate, Forging, Bar
Electrical resistivity		3.45e-08 - 5e-08 Ω·m	T3511	EN 573-3, EN 754	Strip, Sheet, Plate, Forging, Tube, Bar
		4.17e-08 - 4.76e-08 Ω·m	T3511	EN 573-3, EN 754	Strip, Sheet, Plate, Forging, Tube, Bar

Chemical properties

Property	Value	Condition	Related Standards	Shape
Chromium	0.1 %	T3511	EN 573-3, EN 754	Tube, Strip, Sheet, Plate, Forging, Bar
Copper	3.9 - 5.0 %	T3511	EN 573-3, EN 754	Tube, Strip, Sheet, Plate, Forging, Bar
Iron	0.7 %	T3511	EN 573-3	Tube
	0.70 %	T3511	EN 573-3, EN 754	Strip, Sheet, Plate, Forging, Tube, Bar
Magnesium	0.2 - 0.8 %	T3511	EN 573-3, EN 754	Tube, Strip, Sheet, Plate, Forging, Bar
Manganese	0.4 - 1.2 %	T3511	EN 573-3, EN 754	Tube, Strip, Sheet, Plate, Forging, Bar
Silicon	0.5 - 1.2 %	T3511	EN 573-3, EN 754	Tube, Strip, Sheet, Plate, Forging, Bar
Titanium	0.15 %	T3511	EN 573-3, EN 754	Tube, Strip, Sheet, Plate, Forging, Bar
Zinc	0.25 %	T3511	EN 573-3, EN 754	Tube, Strip, Sheet, Plate, Forging, Bar

Technological properties

Property
Anodizing	decorative: not suitable, Protective: acceptable
Brazing	hard brazing (with flux/ without flux): not suitable / not suitable, friction soldering: acceptable, soft brazing with flux: not suitable
Corrosion properties	Seawater: sufficient, weathering: acceptable
Workability	Bending / Spinning (cold): gut (O) / ungeeignet, Impact extrusion (cold): not suitable, Deep drawing / upsetting (Condition) acceptable (O) / not suitable

EN 573-3 AW‑2014 T3510: High‑Strength, Machinable Aluminum Alloy EN AW-2014 T4510 Aluminum Alloy – High Strength & Versatile Performance

Metal