AA 2014 T6510 Aluminum Alloy – Strength, Machinability & Welding Excellence
AA 2014 is an alloy with strength, machinability and welding capabilities, Aluminum Alloy AA 2014 is an excellent option. It is a precipitation hardening alloy that maintains strength after heat treatment.
Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.8 g/cm³ | T6510 | AA Standards, ASTM B241 |
3.0 g/cm³ | T6510 |
Mechanical
| Property | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|
Elastic modulus | 73.0 GPa | T6510 | AA Standards, ASTM B241 | |
Elongation | 5.0 % | T6510 | AA Standards, ASTM B241 | A100 |
6.0 % | T6510 | AA Standards, ASTM B241 | A100 | |
6.1 % | T6510 | |||
7.0 % | T6510 | AA Standards, ASTM B241 | A50 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] | Typical for Wrought 2000 Series Aluminium | ||
Shear modulus | 26.0 - 27.5 GPa | Typical for Wrought 2000 Series Aluminium | ||
Tensile strength | 415.0 MPa | T6510 | AA Standards, ASTM B241 | |
440.0 MPa | T6510 | AA Standards, ASTM B241 | ||
470.0 MPa | T6510 | AA Standards, ASTM B241 | ||
490.0 MPa | T6510 | |||
Yield strength | 365.0 MPa | T6510 | AA Standards, ASTM B241 | RP02 |
400.0 MPa | T6510 | AA Standards, ASTM B241 | RP02 | |
410.0 MPa | T6510 |
Thermal
| Property | Temperature | Value | Condition | Related Standards |
|---|---|---|---|---|
Coefficient of thermal expansion | 2.3e-05 1/K | T6510 | ||
20 °C | 2.3e-05 1/K | T6510 | AA Standards, ASTM B241 | |
100 °C | 2.3e-05 1/K | T6510 | AA Standards, ASTM B241 | |
Melting point | 505.0 - 635.0 °C | T6510 | AA Standards, ASTM B241 | |
510.0 °C | T6510 | |||
Specific heat capacity | 870.0 J/(kg·K) | T6510 | ||
Thermal conductivity | 134.0 - 193.0 W/(m·K) | T6510 | AA Standards, ASTM B241 | |
150.0 W/(m·K) | T6510 |
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 20000000.0 - 29000000.0 S/m | T6510 | AA Standards, ASTM B241 |
Electrical resistivity | 3.45e-08 - 5e-08 Ω·m | T6510 | AA Standards, ASTM B241 |
Chemical properties
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Aluminium | 90.4 - 95.0 % | T6510 | |
Chromium | 0.1 % | T6510 | AA Standards, ASTM B241 |
Copper | 3.9 - 5.0 % | T6510 | AA Standards, ASTM B241 |
Iron | 0.70 % | T6510 | AA Standards, ASTM B241 |
0.7 % | T6510 | ||
Magnesium | 0.2 - 0.8 % | T6510 | AA Standards, ASTM B241 |
Manganese | 0.4 - 1.2 % | T6510 | AA Standards, ASTM B241 |
Other | 0.15 % | T6510 | |
Silicon | 0.5 - 1.2 % | T6510 | AA Standards, ASTM B241 |
Titanium | 0.15 % | T6510 | AA Standards, ASTM B241 |
Zinc | 0.25 % | T6510 | AA Standards, ASTM B241 |
Zirconium | 0.2 % | T6510 |
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: no brazing is known or developed | |
| Corrosion properties | Stress corrosion cracking: Operational damage in areas with tensile stresses transverse to the grain structure, limited damage to laboratory samples, general: sufficient, in principle it should be protected | |
| General machinability | General: poor (O), good to acceptable | |
| Workability | general (condition): poor(T3, T4, T451), not suitable (T6, T651, T6510, T6511) | |
Metal
- AA Standards Grade 6162 T6510 – Key Mechanical Properties & Specifications
- AA 6066 T6510 Aluminium: Standards, Properties & Engineering Specs
- AA 2014 T3 Aluminum Alloy – Premium Strength, Machinability & Welding
- AA 6262 T6510 Aluminum Alloy: High Strength, Excellent Machinability, and Superior Corrosion Resistance
- AA 2014 T4510 Aluminum Alloy: High Strength, Excellent Machinability & Welding
- AA 2014 T4511 Aluminum Alloy – Strength, Machinability & Welding Excellence
- AA 2014 T6511 Aluminum Alloy – Superior Strength & Weldability
- AA 2014 (T652) Aluminum Alloy – Standards and Specifications
- AA 2014 T451 Aluminum Alloy – Grade Standards & Properties
- AA 2014 Aluminum Alloy – Standards, Properties & Applications