ASTM B584 Grade C86400 – Superior Cast Copper Brass
Properties
General
| Property | Value | Comment |
|---|---|---|
Density | 8.47 g/cm³ | Typical for Cast Copper Brass Yellow Brass |
Grain size | 0.0303 μm | Predicted Value |
Mechanical
| Property | Value | Related Standards | Shape | Comment |
|---|---|---|---|---|
Compressive strength | 1162 MPa | Predicted Value | ||
Elastic modulus | 110 - 130 GPa | Typical for Cast Copper Brass Yellow Brass | ||
Fatigue strength | 377 MPa | Predicted Value | ||
Hardness, Brinell | 127 [-] | Predicted Value | ||
Hardness, HBW | 244.4 [-] | Predicted Value | ||
Hardness, Rockwell F | 75 [-] | Predicted Value | ||
Hardness, Rockwell Superficial 15-N | 71 [-] | Predicted Value | ||
Hardness, Rockwell Superficial 30-N | 43 [-] | Predicted Value | ||
Hardness, Rockwell Superficial 30-T | 67 [-] | Predicted Value | ||
Hardness, Vickers | 134 [-] | Predicted Value | ||
Poisson's ratio | 0.34 [-] | Typical for Cast Copper Brass Yellow Brass | ||
Reduction of area | 45.2 % | Predicted Value | ||
Shear modulus | 43.4 GPa | Predicted Value | ||
Shear strength | 280.1 MPa | Predicted Value | ||
Tensile strength | 414 MPa | ASTM B584 | Casting |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 1.5e-05 - 1.9e-05 1/K | Typical for Cast Copper Brass Yellow Brass |
Melting point | 905 - 932 °C | Typical for Cast Copper Brass Yellow Brass |
Specific heat capacity | 335 - 390 J/(kg·K) | Typical for Cast Copper Brass Yellow Brass |
Thermal conductivity | 116 W/(m·K) | Typical for Cast Copper Brass Yellow Brass |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 19 S/m | Predicted Value |
Specific Electrical conductivity | 37 % IACS | Predicted Value |
Chemical properties
| Property | Value | Related Standards | Shape |
|---|---|---|---|
Aluminium | 0.5 - 1.5 % | ASTM B584 | Casting |
Copper | 56 - 62 % | ASTM B584 | Casting |
Iron | 0.4 - 2 % | ASTM B584 | Casting |
Lead | 0.5 - 1.5 % | ASTM B584 | Casting |
Manganese | 0.1 - 1 % | ASTM B584 | Casting |
Nickel | 1 % | ASTM B584 | Casting |
Tin | 0.5 - 1.5 % | ASTM B584 | Casting |
Zinc | 34 - 42 % | ASTM B584 | Casting |
Metal
- ASTM B241 Grade 6066 O – Premium 6066 Aluminum Alloy for Structural Use
- ASTM B241 Grade 6351 T4: Aluminum Tubing – Performance & Standards
- ASTM B241 6351 T6 Aluminium Tubing – Specifications & Performance
- ASTM B241 Grade 6351 T5 – Premium 6000 Series Aluminum Alloy
- ASTM B505 Grade C86200 – Standard for Yellow Brass Cast Copper Brass
- ASTM B505 Grade C86500: Detailed Specifications & Properties
- ASTM B505 Grade C90700 – Key Properties & Mechanical Performance
- ASTM B505 Grade C92700: Detailed Properties & Performance Data
- ASTM B505 Grade C95200: High-Performance Cast Copper Bronze
- ASTM B584 Grade C86700: Properties, Standards & Performance of Yellow Brass