ASTM B584 Grade C86700: Properties, Standards & Performance of Yellow Brass
Properties
General
| Property | Value | Comment |
|---|---|---|
Density | 8.47 g/cm³ | Typical for Cast Copper Brass Yellow Brass |
Grain size | 0.0306 μm | Predicted Value |
Mechanical
| Property | Value | Related Standards | Shape | Comment |
|---|---|---|---|---|
Compressive strength | 1154 MPa | Predicted Value | ||
Elastic modulus | 110 - 130 GPa | Typical for Cast Copper Brass Yellow Brass | ||
Fatigue strength | 379 MPa | Predicted Value | ||
Hardness, Brinell | 146 [-] | Predicted Value | ||
Hardness, HBW | 243.2 [-] | Predicted Value | ||
Hardness, Rockwell F | 78 [-] | Predicted Value | ||
Hardness, Rockwell Superficial 15-N | 71 [-] | Predicted Value | ||
Hardness, Rockwell Superficial 30-N | 43 [-] | Predicted Value | ||
Hardness, Rockwell Superficial 30-T | 75 [-] | Predicted Value | ||
Hardness, Vickers | 143 [-] | Predicted Value | ||
Poisson's ratio | 0.34 [-] | Typical for Cast Copper Brass Yellow Brass | ||
Reduction of area | 36.4 % | Predicted Value | ||
Shear modulus | 42.9 GPa | Predicted Value | ||
Shear strength | 313.3 MPa | Predicted Value | ||
Tensile strength | 552 MPa | ASTM B584 | Casting |
Thermal
| Property | Value | Comment |
|---|---|---|
Coefficient of thermal expansion | 1.5e-05 - 1.9e-05 1/K | Typical for Cast Copper Brass Yellow Brass |
Melting point | 905 - 932 °C | Typical for Cast Copper Brass Yellow Brass |
Specific heat capacity | 335 - 390 J/(kg·K) | Typical for Cast Copper Brass Yellow Brass |
Thermal conductivity | 116 W/(m·K) | Typical for Cast Copper Brass Yellow Brass |
Electrical
| Property | Value | Comment |
|---|---|---|
Electrical conductivity | 17 S/m | Predicted Value |
Specific Electrical conductivity | 36 % IACS | Predicted Value |
Chemical properties
| Property | Value | Related Standards | Shape |
|---|---|---|---|
Aluminium | 1 - 3 % | ASTM B584 | Casting |
Copper | 55 - 60 % | ASTM B584 | Casting |
Iron | 1 - 3 % | ASTM B584 | Casting |
Lead | 0.5 - 1.5 % | ASTM B584 | Casting |
Manganese | 1 - 3.5 % | ASTM B584 | Casting |
Nickel | 1 % | ASTM B584 | Casting |
Tin | 1.5 % | ASTM B584 | Casting |
Zinc | 30 - 38 % | ASTM B584 | Casting |
Metal
- ASTM B241 Grade 6066 O – Premium 6066 Aluminum Alloy for Structural Use
- ASTM B241 Grade 6351 T4: Aluminum Tubing – Performance & Standards
- ASTM B241 6351 T6 Aluminium Tubing – Specifications & Performance
- ASTM B241 Grade 6351 T5 – Premium 6000 Series Aluminum Alloy
- ASTM B505 Grade C86200 – Standard for Yellow Brass Cast Copper Brass
- ASTM B505 Grade C86500: Detailed Specifications & Properties
- ASTM B505 Grade C90700 – Key Properties & Mechanical Performance
- ASTM B505 Grade C92700: Detailed Properties & Performance Data
- ASTM B505 Grade C95200: High-Performance Cast Copper Bronze
- ASTM B584 Grade C86400 – Superior Cast Copper Brass