5182 H48 Non-Heat-Treatable Aluminum Wrought Alloy – Formability & Strength
Good combination of formability and strength.
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 23.0 °C | 2.65 g/cm³ |
Dimension
| Property | Value |
|---|---|
Thickness | 0.2 - 0.35 mm |
Mechanical
| Property | Temperature | Value |
|---|---|---|
Elastic modulus | 23.0 °C | 71 GPa |
Elongation A50 | 23.0 °C | 1 % |
Hardness, HBW | 23.0 °C | 114 [-] |
Shear modulus | 23.0 °C | 27 GPa |
Tensile strength | 23.0 °C | 380 MPa |
Yield strength | 23.0 °C | 320 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 100.0 °C | 2.4E-5 1/K | 20-100°C |
Thermal conductivity | 23.0 °C | 121 W/(m·K) |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical resistivity | 23.0 °C | 5.6E-8 Ω·m |
Chemical properties
| Property | Value |
|---|---|
Chromium | 0.1 % |
Copper | 0.15 % |
Iron | 0.35 % |
Magnesium | 4 - 5 % |
Manganese | 0.2 - 0.5 % |
Other | 0.05 - 0.15 % |
Silicon | 0.2 % |
Titanium | 0.1 % |
Zinc | 0.25 % |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | Excellent | |
| Application areas | Wind energy: Nacelle coverings, rotor hub, stairs; Components: Heat shields, Access hatches, Spoilers, General tranportation | |
| Brazing | Brazing is not recommended. | |
| Corrosion properties | Excellent | |
| Welding | Good | |
| Workability | Very good in special (Lüder lines resistant) O temper. | |
Metal
- 1085A O: Premium Non-Heat-Treatable Aluminum Wrought Alloy – Exceptional Surface Finish & Corrosion Resistance
- 1085O Non-Heat Treatable Aluminum Wrought Alloy – Superior Surface Finish & Mechanical Performance
- 1090O Aluminium Alloy – Non‑Heat Treated Wrought Material with Superior Surface Finish
- Aluminium Alloy 5042O – High-Strength, Non‑Heat‑Treatable Wrought Metal
- 1100 O Aluminum Wrought Alloy – Non‑Heat‑Treatable, Superior Corrosion Resistance & Workability
- 5005A O – Non-Heat-Treatable Aluminum Wrought Alloy: Work-Hardenable for Matte Finishes
- Aluminum 1350O Wrought Alloy – Non-Heat Treated, Excellent Conductivity
- 5182 H19 Non-Heat Treatable Aluminum Wrought Alloy – High Strength & Formability
- 3005 O Aluminum Wrought Alloy – Non‑Heat Treated, Medium Strength & Corrosion Resistant
- 3105A O: Non-Heat-Treatable Aluminum Wrought Alloy – Strength, Corrosion Resistance & Key Properties