5086 H16 Aluminum Wrought Alloy – Non‑Heat‑Treatable, Superior Corrosion Resistance
High corrosion resistance against seawater.
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 23.0 °C | 2.66 g/cm³ |
Dimension
| Property | Value |
|---|---|
Thickness | 0.2 - 4 mm |
Mechanical
| Property | Temperature | Value |
|---|---|---|
Elastic modulus | 23.0 °C | 71 GPa |
Elongation A50 | 23.0 °C | 1 - 2 % |
Hardness, HBW | 23.0 °C | 98 [-] |
Shear modulus | 23.0 °C | 27 GPa |
Tensile strength | 23.0 °C | 325 - 385 MPa |
Yield strength | 23.0 °C | 270 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 100.0 °C | 2.4E-5 1/K | 20-100°C |
Thermal conductivity | 23.0 °C | 126 W/(m·K) |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical resistivity | 23.0 °C | 5.6E-8 Ω·m |
Chemical properties
| Property | Value |
|---|---|
Chromium | 0.05 - 0.25 % |
Copper | 0.1 % |
Iron | 0.5 % |
Magnesium | 3.5 - 4.5 % |
Manganese | 0.2 - 0.7 % |
Other | 0.05 - 0.15 % |
Silicon | 0.4 % |
Titanium | 0.15 % |
Zinc | 0.25 % |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | Excellent (anodizing quality) | |
| Application areas | Vessels: Pressure, Cryogenics; Components: Access hatches, Spoilers, General tranportation | |
| Corrosion properties | Excellent | |
| Welding | Good | |
| Workability | Good (in O temper) | |
Metal
- 1085A O: Premium Non-Heat-Treatable Aluminum Wrought Alloy – Exceptional Surface Finish & Corrosion Resistance
- 1085O Non-Heat Treatable Aluminum Wrought Alloy – Superior Surface Finish & Mechanical Performance
- 5086 H36 Non-Heat-Treated Aluminum Wrought Alloy – Exceptional Corrosion Resistance
- 5086 H18 Aluminum Wrought Alloy – Non-Heat-Treatable, Superior Corrosion Resistance
- 5052 H16 Non-Heat-Treatable Aluminum Wrought Alloy – High Strength & Corrosion Resistance
- 5086 H12 Aluminium Wrought Alloy – Non-Heat Treatable with Superior Corrosion Resistance
- 5086 H14 Non-Heat-Treatable Aluminum Wrought Alloy – High Corrosion Resistance & Mechanical Strength
- 5086 H26 Aluminum Wrought Alloy - Superior Corrosion Resistance
- 5251 H16 Aluminium Wrought Alloy – Non-Heat-Treatable, Medium Strength & Excellent Corrosion Resistance
- 5049 H16: Reliable Non-Heat-Treatable Aluminum Alloy for Superior Durability