8006 O Alloy: High-Strength, Non-Heat Treatable Aluminum Wrought Material
High strength when compared to 1xxx in foil app. Alloy 8006 can be welded, adhesive bonded, and formed easily. It offers a useful combination of strength and ductility at room temperature while retaining its strength at elevated temperatures.
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 23.0 °C | 2.74 g/cm³ |
Dimension
| Property | Value |
|---|---|
Thickness | 0.06 - 0.2 mm |
Mechanical
| Property | Temperature | Value |
|---|---|---|
Elastic modulus | 23.0 °C | 70 GPa |
Elongation A50 | 23.0 °C | 14 % |
Shear modulus | 23.0 °C | 25 GPa |
Tensile strength | 23.0 °C | 90 - 140 MPa |
Yield strength | 23.0 °C | 100 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 100.0 °C | 2.4E-5 1/K | 20-100°C |
Thermal conductivity | 23.0 °C | 190 - 210 W/(m·K) |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical resistivity | 23.0 °C | 3.1E-8 Ω·m |
Chemical properties
| Property | Value |
|---|---|
Copper | 0.3 % |
Iron | 1.2 - 2 % |
Magnesium | 0.1 % |
Manganese | 0.3 - 1 % |
Silicon | 0.4 % |
Zinc | 0.1 % |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | Limited | |
| Application areas | Facades: Single sheet, Sheets for composites/ sandwich Panels; Roofing: Foil for bituminous coating; Doors: Sheets for composites/ sandwich Panels; Electronic devices: Housing of devices; Heat exchangers: Fins, Heat exchangers, General applications; Tubes: Industrial tubes, Flexible tubes, Pipes; Insulation; Semi-rigid and corrugated: Pet food, Smooth wall; Components: Automotive fins, Heat exchangers | |
| Corrosion properties | Limited | |
| Welding | Good | |
| Workability | Very Good | |
Metal
- 1085A O: Premium Non-Heat-Treatable Aluminum Wrought Alloy – Exceptional Surface Finish & Corrosion Resistance
- 8079 H19 Non-Heat Treatable Aluminum Wrought Alloy – Superior Strength & Formability
- 1085O Non-Heat Treatable Aluminum Wrought Alloy – Superior Surface Finish & Mechanical Performance
- 1090O Aluminium Alloy – Non‑Heat Treated Wrought Material with Superior Surface Finish
- Aluminium Alloy 5042O – High-Strength, Non‑Heat‑Treatable Wrought Metal
- 1100 O Aluminum Wrought Alloy – Non‑Heat‑Treatable, Superior Corrosion Resistance & Workability
- 5005A O – Non-Heat-Treatable Aluminum Wrought Alloy: Work-Hardenable for Matte Finishes
- Aluminum 1350O Wrought Alloy – Non-Heat Treated, Excellent Conductivity
- 8006 H24 Aluminium Wrought Alloy: High Strength, Easy Fabrication, Non-Heat Treatable
- 3005 O Aluminum Wrought Alloy – Non‑Heat Treated, Medium Strength & Corrosion Resistant