8006 H24 Aluminium Wrought Alloy: High Strength, Easy Fabrication, Non-Heat Treatable

High strength when compared to 1xxx in foil app. Alloy 8006 can be welded, adhesive bonded, and formed easily. It offers a useful combination of strength and ductility at room temperature while retaining its strength at elevated temperatures.

Properties

General

Property	Temperature	Value
Density	23.0 °C	2.74 g/cm³

Dimension

Property	Value
Thickness	0.06 - 0.2 mm

Mechanical

Property	Temperature	Value
Elastic modulus	23.0 °C	70 GPa
Elongation A50	23.0 °C	5 %
Shear modulus	23.0 °C	25 GPa
Tensile strength	23.0 °C	110 - 170 MPa
Yield strength	23.0 °C	90 MPa

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	100.0 °C	2.4E-5 1/K	20-100°C
Thermal conductivity	23.0 °C	190 - 210 W/(m·K)

Electrical

Property	Temperature	Value
Electrical resistivity	23.0 °C	3.1E-8 Ω·m

Chemical properties

Property	Value
Copper	0.3 %
Iron	1.2 - 2 %
Magnesium	0.1 %
Manganese	0.3 - 1 %
Silicon	0.4 %
Zinc	0.1 %

Technological properties

Property
Anodizing	Limited
Application areas	Facades: Single sheet, Sheets for composites/ sandwich Panels; Roofing: Foil for bituminous coating; Doors: Sheets for composites/ sandwich Panels; Electronic devices: Housing of devices; Heat exchangers: Fins, Heat exchangers, General applications; Tubes: Industrial tubes, Flexible tubes, Pipes; Insulation; Semi-rigid and corrugated: Pet food, Smooth wall; Components: Automotive fins, Heat exchangers
Corrosion properties	Limited
Welding	Good
Workability	Very Good