3105A H19: High-Performance Non-Heat-Treatable Aluminum Wrought Alloy
A low to medium strength alloy with good corrosion resistance.
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 23.0 °C | 2.71 g/cm³ |
Dimension
| Property | Value |
|---|---|
Thickness | 0.2 - 2 mm |
Mechanical
| Property | Temperature | Value |
|---|---|---|
Bending angle 180° | 23.0 °C | 0 °/t |
Elastic modulus | 23.0 °C | 69 GPa |
Hardness, HBW | 23.0 °C | 60 [-] |
Shear modulus | 23.0 °C | 26 GPa |
Tensile strength | 23.0 °C | 100 MPa |
Yield strength | 23.0 °C | 40 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 100.0 °C | 2.4E-5 1/K | 20-100°C |
Thermal conductivity | 23.0 °C | 172 W/(m·K) |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical resistivity | 23.0 °C | 3.8E-8 Ω·m |
Chemical properties
| Property | Value |
|---|---|
Chromium | 0.2 % |
Copper | 0.3 % |
Iron | 0.7 % |
Magnesium | 0.2 - 0.8 % |
Manganese | 0.3 - 0.8 % |
Silicon | 0.6 % |
Zinc | 0.25 % |
Technological properties
| Property | ||
|---|---|---|
| Anodizing | Good | |
| Application areas | Closures: Short cups; Food can: Body, Lids; Semi-rigid and corrugated: Pet food | |
| Brazing | Good | |
| Corrosion properties | Very Good | |
| Welding | Very Good | |
| Workability | Very Good | |
3105A O: Non-Heat-Treatable Aluminum Wrought Alloy – Strength, Corrosion Resistance & Key Properties
5049 H12 – High-Performance Non‑Heat‑Treatable Aluminum Wrought Alloy
Metal
- 8079 H19 Non-Heat Treatable Aluminum Wrought Alloy – Superior Strength & Formability
- 1350 H19 Non-Heat-Treatable Al Wrought Alloy – High Conductivity & Mechanical Strength
- 3105A H28 Non-Heat-Treatable Aluminum Alloy – Low‑to‑Medium Strength, Superior Corrosion Resistance
- 5154A H19 Aluminum Wrought Alloy – Non‑Heat‑Treatable, High Strength & Corrosion‑Resistant
- 5182 H19 Non-Heat Treatable Aluminum Wrought Alloy – High Strength & Formability
- 1050A H19 Non-Heat-Treatable Aluminum Wrought Alloy – Superior Corrosion Resistance & Conductivity
- 3103 H19 Non-Heat-Treatable Aluminum Wrought Alloy: Superior Strength & Corrosion Resistance
- 3105A H14 Aluminum Wrought Alloy – Non‑Heat Treatable, Corrosion‑Resistant & Versatile
- 3105A H24 – Premium Non‑Heat‑Treatable Aluminum Alloy
- 3105A O: Non-Heat-Treatable Aluminum Wrought Alloy – Strength, Corrosion Resistance & Key Properties