EN 573-3 Grade AW-5005 (H46) – Lightweight, Corrosion‑Resistant Aluminum Alloy

Aluminum EN AW-5005 is a lean aluminum magnesium alloy with low density and excellent thermal conductivity. This medium strength non-heat-treatable alloy is known for its corrosion resistance in alkaline marine situations. Aluminum EN AW-5005 is readily machinable, and can be welded using TIG and MIG methods. It is important to note that anodizing is a critical part to how Aluminum EN AW-5005 is used.

Properties

General

Property	Temperature	Value	Condition	Related Standards	Shape
Density		2.7 g/cm³	H46	EN 573-3, EN 1396	Strip, Sheet, Plate, Tube, Welded Tube, Bar
	20.0 °C	2.7 g/cm³	H46	EN 573-3	Sheet, Strip

Mechanical

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Elastic modulus		69.0 GPa	H46	EN 573-3, EN 1396	Strip, Sheet, Plate, Tube, Welded Tube, Bar
		69.5 GPa	H46	EN 573-3, EN 1396	Strip, Sheet, Plate, Tube, Welded Tube, Bar
	20.0 °C	69.5 GPa	H46	EN 573-3	Sheet, Strip
Plane-Strain Fracture Toughnes		22.0 - 35.0 MPa·√m				Typical for Wrought 5000 Series Aluminium
Poisson's ratio	20.0 °C	0.33 [-]	H46	EN 573-3	Sheet, Strip
Shear modulus		26.1 GPa	H46	EN 573-3, EN 1396	Strip, Sheet, Plate, Tube, Welded Tube, Bar
	20.0 °C	26.1 GPa	H46	EN 573-3	Sheet, Strip
Tensile strength	20.0 °C	165.0 - 205.0 MPa	H46	EN 573-3	Sheet, Strip	Transverse
	20.0 °C	165.0 - 205.0 MPa	H46	EN 573-3, EN 1396	Strip, Sheet, Plate, Tube, Welded Tube, Bar

Thermal

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Coefficient of thermal expansion	20 °C	2.38e-05 1/K	H46	EN 573-3, EN 1396	Strip, Sheet, Plate, Tube, Welded Tube, Bar
	100 °C	2.38e-05 1/K	H46	EN 573-3, EN 1396	Strip, Sheet, Plate, Tube, Welded Tube, Bar
Max service temperature		150.0 °C				Typical for Wrought 5000 Series Aluminium
Melting point		630.0 - 655.0 °C	H46	EN 573-3, EN 1396	Strip, Sheet, Plate, Tube, Welded Tube, Bar
Specific heat capacity	20.0 °C	897.0 J/(kg·K)	H46	EN 573-3	Sheet, Strip
Thermal conductivity		201 W/(m·K)	H46	EN 573-3, EN 1396	Strip, Sheet, Plate, Tube, Welded Tube, Bar
	20.0 °C	201.0 W/(m·K)	H46	EN 573-3	Sheet, Strip

Electrical

Property	Temperature	Value	Condition	Related Standards	Shape
Electrical conductivity		30000000.0 S/m	H46	EN 573-3, EN 1396	Strip, Sheet, Plate, Tube, Welded Tube, Bar
Electrical resistivity		3.33e-08 Ω·m	H46	EN 573-3, EN 1396	Strip, Sheet, Plate, Tube, Welded Tube, Bar
	20.0 °C	3.3e-08 Ω·m	H46	EN 573-3	Sheet, Strip

Chemical properties

Property	Value	Condition	Related Standards	Shape
Chromium	0.1 %	H46	EN 573-3, EN 1396	Sheet, Strip, Plate, Tube, Welded Tube, Bar
Copper	0.2 %	H46	EN 573-3, EN 1396	Sheet, Strip, Plate, Tube, Welded Tube, Bar
Iron	0.7 %	H46	EN 573-3	Sheet, Strip
	0.70 %	H46	EN 573-3, EN 1396	Strip, Sheet, Plate, Tube, Welded Tube, Bar
Magnesium	0.5 - 1.1 %	H46	EN 573-3, EN 1396	Sheet, Strip, Plate, Tube, Welded Tube, Bar
Manganese	0.2 %	H46	EN 573-3, EN 1396	Sheet, Strip, Plate, Tube, Welded Tube, Bar
Silicon	0.3 %	H46	EN 573-3, EN 1396	Sheet, Strip, Plate, Tube, Welded Tube, Bar
Zinc	0.25 %	H46	EN 573-3, EN 1396	Sheet, Strip, Plate, Tube, Welded Tube, Bar

Technological properties

Property
Anodizing	decorative: acceptable, Protective: very good
Brazing	hard brazing (with flux/ without flux): acceptable / sufficient, friction soldering: good, soft brazing with flux: sufficient
Corrosion properties	Seawater: good, weathering: very good
Workability	Bending / Spinning (cold): good / acceptable, Impact extrusion (cold): acceptable, Deep drawing / upsetting (Condition) good (O) / good (O)