BP11NPG Phenolic Sheet with Graphite Lubricant – High Wear Resistance
Canvas phenolic laminate with graphite added as a solid lubricant. This material has improved wear properties under certain conditions.
Properties
General
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Bonding strength | 816.5 Kg | ASTM D229 | Condition A |
Density | 1.4 g/cm³ | ASTM D792 | |
Moisture absorption | 2.2 % | ASTM D570 | Condition A |
Mechanical
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Compressive strength | 262 MPa | ASTM D695 | Condition A | Flatwise |
Flexural modulus | 6.9 GPa | ASTM D790 | Condition A, Transverse |
8.3 GPa | ASTM D790 | Condition A | |
Flexural strength | 103.4 MPa | ASTM D790 | Condition A, Transverse |
131 MPa | ASTM D790 | Condition A | |
Hardness, Rockwell M | 90 [-] | ASTM D785 | |
Impact strength, Izod unnotched, ASTM | 75 J/m | ASTM D256 | Condition E-48/50, Transverse |
91 J/m | ASTM D256 | Condition E-48/50 | |
Shear strength | 89.6 MPa | ASTM D732 | Condition A, Transverse |
Tensile strength | 68.9 MPa | ASTM D638 | Condition A |
Thermal
| Property | Value | Testing Standard | Comment | ||
|---|---|---|---|---|---|
Coefficient of thermal expansion | 1.8e-05 1/K | IPC-TM 650-2.4.24 | |||
2.4e-05 1/K | IPC-TM 650-2.4.24 | Transverse | |||
Relative temperature index, mechanical strength | 125 °C | UL Bulletin 746b¹ | |||
Flammability | UL Bulletin 94, Class HB, Condition A | ||||
Technological properties
| Property | ||
|---|---|---|
| Application areas | Material is conductive to electricity and should not be used where this is detrimental to the application. | |
| Fillers | Cotton Fabric and Graphite Powder | |
| Other | 1.This temperature is a recommendation only, and based upon experience in various applications. The maximum operating temperature is dependent upon the application and should be investigated prior to use | |
| Supplier Disclaimer | This data, while believed to be accurate and based on reliable analytical methods, is for informational purposes only. The terms and conditions of the agreement under which it is sold will govern any sales of this product. Data supplied above are "typical values"; not to be considered "specification values". To assure the material's performance is adequate for a specific application; customers should verify, independent of Norplex-Micarta, performance characteristics of interest. It is the responsibility of the users of this information to make sure that they have the latest version of this TDB, and are urged to check with Customer Service or, preferably our web site, www.norplex-micarta.com, to determine if the information is the most current available. | |
Composite material
- BP11MPN Phenolic Composite Sheet – Superior Medium‑Weave Cotton Performance
- MC223 Medium-Weave Cotton Phenolic Sheet – High Performance Composite
- NP313HT Phenolic Sheet – Durable, Semi-Conductive, Low-Wear Performance
- BP13HPM Phenolic Sheet – High‑Performance Molybdenum‑Disulphide Laminated Material
- BP14NPG Phenolic Sheet – Superior Wear-Resistant, High-Performance Material
- NP611R Phenolic Sheet – High Performance, Superior Electrical & Moisture Resistance
- Phenolic NP631 Sheet: Superior Hot Punching Grade with Excellent Electrical Properties
- NP625 Phenolic Sheet: Superior Electrical Performance & Robust Bonding
- Phenolic NP630 Sheet – Superior Machining Grade with Exceptional Electrical and Moisture Resistance
- NP611 Phenolic Sheet – Superior Electrical & Moisture Resistance