ASTM A473 Grade S41425 Tempered Stainless Steel – High Strength, Reliable Performance

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	7.6 - 7.7 g/cm³	Typical for Martensitic Stainless Steel

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	220 GPa	Typical for Martensitic Stainless Steel
Elongation A50	23.0 °C	15 %
Hardness, Brinell	23.0 °C	321 [-]
Poisson's ratio	23.0 °C	0.3 [-]	Typical for Martensitic Stainless Steel
Reduction of area	23.0 °C	45 %
Shear modulus	23.0 °C	77 GPa	Typical for Martensitic Stainless Steel
Tensile strength	23.0 °C	825 MPa
Yield strength Rp0.2	23.0 °C	655 MPa

Thermal

Property	Temperature	Value	Comment
Coefficient of thermal expansion	23.0 °C	1E-5 - 1.5E-5 1/K	Typical for Martensitic Stainless Steel
Melting point		1370 - 1530 °C	Typical for Martensitic Stainless Steel
Specific heat capacity	23.0 °C	460 J/(kg·K)	Typical for Martensitic Stainless Steel
Thermal conductivity	23.0 °C	14 - 31 W/(m·K)	Typical for Martensitic Stainless Steel

Electrical

Property	Temperature	Value	Comment
Electrical resistivity	23.0 °C	6E-7 Ω·m	Typical for Martensitic Stainless Steel

Chemical properties

Property	Value
Carbon	0.05 %
Chromium	12 - 15 %
Manganese	0.5 - 1 %
Molybdenum	1.5 - 2 %
Nickel	4 - 7 %
Nitrogen	0.06 - 0.12 %
Phosphorus	0.02 %
Silicon	0.5 %
Sulfur	5E-3 %