VdTÜV WB 230-3 Ti3 Grade Titanium – High-Strength, Welded Form

DIN Ti3 titanium is the third of four commercially unalloyed titanium grades. It is known for its high strength and good corrosion resistance. It also has good impact properties at low temperature and is suitable for being welded, machined, cold worked and cast.

Properties

General

Property	Temperature	Value	Condition	Related Standards	Shape
Density	20.0 °C	4.505 g/cm³	Welded	VdTÜV WB 230-3, DIN 17850, DIN 17862, DIN 17864, DIN 17860, VdTÜV WB 230-1, VdTÜV WB 230-2	Forging, Rod, Wire, Tube, Flat

Mechanical

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Elastic modulus	20.0 °C	108.0 - 110.0 GPa	Welded	VdTÜV WB 230-3, DIN 17850, DIN 17862, DIN 17864, DIN 17860, VdTÜV WB 230-1, VdTÜV WB 230-2	Forging, Rod, Wire, Tube, Flat
	200.0 °C	96.0 - 97.0 GPa	Welded	VdTÜV WB 230-3, DIN 17850, DIN 17862, DIN 17864, DIN 17860, VdTÜV WB 230-1, VdTÜV WB 230-2	Forging, Rod, Wire, Tube, Flat
	400.0 °C	82.0 GPa	Welded	VdTÜV WB 230-3, DIN 17850, DIN 17862, DIN 17864, DIN 17860, VdTÜV WB 230-1, VdTÜV WB 230-2	Forging, Rod, Wire, Tube, Flat
Poisson's ratio		0.361 [-]				Typical for Pure Titanium
Shear modulus		46.0 GPa				Typical for Pure Titanium

Thermal

Property	Temperature	Value	Condition	Related Standards	Shape	Comment
Coefficient of thermal expansion		8.400000000000001e-06 - 8.599999999999999e-06 1/K				Typical for Pure Titanium
Melting point		1670.0 °C				Typical for Pure Titanium
Specific heat capacity	20.0 °C	520.0 J/(kg·K)	Welded	VdTÜV WB 230-3, DIN 17850, DIN 17862, DIN 17864, DIN 17860, VdTÜV WB 230-1, VdTÜV WB 230-2	Forging, Rod, Wire, Tube, Flat
	200.0 °C	570.0 J/(kg·K)	Welded	VdTÜV WB 230-3, DIN 17850, DIN 17862, DIN 17864, DIN 17860, VdTÜV WB 230-1, VdTÜV WB 230-2	Forging, Rod, Wire, Tube, Flat
	400.0 °C	630.0 J/(kg·K)	Welded	VdTÜV WB 230-3, DIN 17850, DIN 17862, DIN 17864, DIN 17860, VdTÜV WB 230-1, VdTÜV WB 230-2	Forging, Rod, Wire, Tube, Flat
Thermal conductivity	20.0 °C	22.6 W/(m·K)	Welded	VdTÜV WB 230-3, DIN 17850, DIN 17862, DIN 17864, DIN 17860, VdTÜV WB 230-1, VdTÜV WB 230-2	Forging, Rod, Wire, Tube, Flat
	200.0 °C	20.9 W/(m·K)	Welded	VdTÜV WB 230-3, DIN 17850, DIN 17862, DIN 17864, DIN 17860, VdTÜV WB 230-1, VdTÜV WB 230-2	Forging, Rod, Wire, Tube, Flat
	400.0 °C	19.3 W/(m·K)	Welded	VdTÜV WB 230-3, DIN 17850, DIN 17862, DIN 17864, DIN 17860, VdTÜV WB 230-1, VdTÜV WB 230-2	Forging, Rod, Wire, Tube, Flat

Electrical

Property	Temperature	Value	Condition	Related Standards	Shape
Electrical resistivity	20.0 °C	5.2e-07 Ω·m	Welded	VdTÜV WB 230-3, DIN 17850, DIN 17862, DIN 17864, DIN 17860, VdTÜV WB 230-1, VdTÜV WB 230-2	Forging, Rod, Wire, Tube, Flat
	200.0 °C	8.7e-07 Ω·m	Welded	VdTÜV WB 230-3, DIN 17850, DIN 17862, DIN 17864, DIN 17860, VdTÜV WB 230-1, VdTÜV WB 230-2	Forging, Rod, Wire, Tube, Flat
	400.0 °C	1.2e-06 Ω·m	Welded	VdTÜV WB 230-3, DIN 17850, DIN 17862, DIN 17864, DIN 17860, VdTÜV WB 230-1, VdTÜV WB 230-2	Forging, Rod, Wire, Tube, Flat

Chemical properties

Property	Value	Condition	Related Standards	Shape
Carbon	0.06	Welded	VdTÜV WB 230-3, DIN 17850, DIN 17862, DIN 17864, DIN 17860, VdTÜV WB 230-1, VdTÜV WB 230-2	Forging, Rod, Wire, Tube, Flat
Hydrogen	0.013	Welded	VdTÜV WB 230-3, DIN 17850, DIN 17862, DIN 17864, DIN 17860, VdTÜV WB 230-1, VdTÜV WB 230-2	Forging, Rod, Wire, Tube, Flat
Iron	0.25	Welded	VdTÜV WB 230-3, DIN 17850, DIN 17862, DIN 17864, DIN 17860, VdTÜV WB 230-1, VdTÜV WB 230-2	Forging, Rod, Wire, Tube, Flat
Nitrogen	0.05	Welded	VdTÜV WB 230-3, DIN 17850, DIN 17862, DIN 17864, DIN 17860, VdTÜV WB 230-1, VdTÜV WB 230-2	Forging, Rod, Wire, Tube, Flat
Oxygen	0.25	Welded	VdTÜV WB 230-3, DIN 17850, DIN 17862, DIN 17864, DIN 17860, VdTÜV WB 230-1, VdTÜV WB 230-2	Forging, Rod, Wire, Tube, Flat
Titanium	99.0 %	Welded	DIN 17850, VdTÜV WB 230-2, VdTÜV WB 230-1, VdTÜV WB 230-3, DIN 17862, DIN 17864, DIN 17860	Tube, Flat, Forging, Rod, Wire