EN 1652 Grade CuSn3Zn9 H080 – Superior Copper‑Tin Alloy for Electrical Engineering
Material CuSn3Zn9, mat. No. CW454K, is predominantly used in electrical engineering. The multicomponent alloy is characterized by a considerably lower stress corrosion sensitivity compared to the copper-zinc-alloys. The spring properties come up to alloy CuSn4 (CW450K). For the electrolytically tinned strip the coatings (Sn bright, Sn matt, Sn fuzed, SnPb) are listed by the application (better solderability, better corrosion resistance, reduction of the electrical contact resistance, better appearance) in the DIN EN 14436 : 2004-11 (Table 5)
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 8.75 - 8.8 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 20.0 °C | 126 GPa | |
Hardness, Vickers | 20.0 °C | 80 - 110 [-] | |
Poisson's ratio | 20.0 °C | 0.34 [-] | |
Shear modulus | 23.0 °C | 40 GPa | Typical for Wrought Copper Brass |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 100.0 °C | 1.83E-5 1/K | |
300.0 °C | 1.85E-5 1/K | ||
Melting point | 875 - 1075 °C | Typical for Wrought Copper Brass | |
Specific heat capacity | 20.0 °C | 380 J/(kg·K) | |
200.0 °C | 410 J/(kg·K) | ||
Thermal conductivity | 20.0 °C | 120 W/(m·K) | |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical conductivity | 20.0 °C | 1.60E+7 S/m |
Specific Electrical conductivity | 28 % IACS |
Chemical properties
| Property | Value |
|---|---|
Iron | 0.1 % |
Lead | 0.1 % |
Nickel | 0.2 % |
Phosphorus | 0.2 % |
Tin | 1.5 - 3.5 % |
Zinc | 7.5 - 10 % |
Metal
- EN 1652 CuSn3Zn9 Alloy – H110 Grade for Electrical Engineering
- EN 1652 Grade CuSn3Zn9 H140 – High-Performance Copper‑Tin‑Zinc Alloy for Electrical Engineering
- EN 1652 Grade CuSn3Zn9 H160 – High-Performance Copper Tin Alloy for Electrical Engineering
- EN 1652 Grade CuSn3Zn9 H180: High-Performance Copper-Sn-Zn Alloy
- EN 1652 Grade CuSn3Zn9 – High‑Performance Copper Alloy for Electrical Applications
- EN 1652 Grade CuZn10 H080 – High-Performance Wrought Copper Alloy
- EN 1652 Grade CuSn6 H080 – Premium Tin-Copper Alloy with Enhanced Corrosion Resistance
- EN 1652 Grade CuSn3Zn9 R510 – High‑Performance, Low Stress‑Corrosion Alloy for Electrical Engineering
- EN 1652 Grade CuSn3Zn9 R580 – High-Performance Cu‑Sn‑Zn Alloy for Electrical Applications
- EN 1652 Grade CuSn3Zn9 R660 – High-Performance Copper–Tin–Zinc Alloy for Electrical Engineering