DIN 1652-3 Grade 20MoCrS4 Cold-Drawn Steel: Ideal for Wear-Resistant Mechanical Components
The steel 20 MoCrS 4 is used for wear loaded parts in the vehicle and mechanical engineering with medium core strength, better machinability, high toughness and high fatigue strength (e.g. gears, shafts, axles). The lowest application amounts to -60 °C, the best application up to 60 mm nominal size.
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 7.83 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | -100.0 °C | 217 GPa | |
20.0 °C | 212 GPa | ||
100.0 °C | 207 GPa | ||
200.0 °C | 199 GPa | ||
300.0 °C | 192 GPa | ||
400.0 °C | 184 GPa | ||
500.0 °C | 175 GPa | ||
600.0 °C | 164 GPa | ||
Poisson's ratio | 23.0 °C | 0.29 [-] | Typical for Chromium Molybdenum Steel |
Tensile strength | 20.0 °C | 720 - 800 MPa | |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | -100.0 °C | 1.05E-5 1/K | |
20.0 °C | 1.15E-5 1/K | ||
100.0 °C | 1.21E-5 1/K | ||
200.0 °C | 1.27E-5 1/K | ||
300.0 °C | 1.32E-5 1/K | ||
400.0 °C | 1.36E-5 1/K | ||
500.0 °C | 1.4E-5 1/K | ||
600.0 °C | 1.44E-5 1/K | ||
Max service temperature, long | -60 - 0 °C | ||
Melting point | 1382 - 1529 °C | Typical for Chromium Molybdenum Steel | |
Specific heat capacity | -100.0 °C | 423 J/(kg·K) | |
20.0 °C | 461 J/(kg·K) | ||
100.0 °C | 479 J/(kg·K) | ||
200.0 °C | 499 J/(kg·K) | ||
300.0 °C | 517 J/(kg·K) | ||
400.0 °C | 536 J/(kg·K) | ||
500.0 °C | 558 J/(kg·K) | ||
600.0 °C | 587 J/(kg·K) | ||
Thermal conductivity | 20.0 °C | 41 W/(m·K) | |
100.0 °C | 42.7 W/(m·K) | ||
200.0 °C | 42.8 W/(m·K) | ||
300.0 °C | 41.6 W/(m·K) | ||
400.0 °C | 39.9 W/(m·K) | ||
500.0 °C | 37.8 W/(m·K) | ||
600.0 °C | 35.6 W/(m·K) | ||
Thermal diffusivity | 20.0 °C | 11.4 mm²/s | |
100.0 °C | 11 mm²/s | ||
200.0 °C | 10.3 mm²/s | ||
300.0 °C | 9.5 mm²/s | ||
400.0 °C | 8.5 mm²/s | ||
500.0 °C | 7.3 mm²/s | ||
600.0 °C | 6 mm²/s | ||
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical resistivity | 20.0 °C | 2.54E-7 Ω·m |
100.0 °C | 3E-7 Ω·m | |
200.0 °C | 3.69E-7 Ω·m | |
300.0 °C | 4.51E-7 Ω·m | |
400.0 °C | 5.45E-7 Ω·m | |
500.0 °C | 6.54E-7 Ω·m | |
600.0 °C | 7.78E-7 Ω·m | |
Chemical properties
| Property | Value |
|---|---|
Carbon | 0.17 - 0.22 % |
Chromium | 0.3 - 0.6 % |
Manganese | 0.7 - 1 % |
Molybdenum | 0.4 - 0.5 % |
Phosphorus | 0.04 % |
Silicon | 0.4 % |
Sulfur | 0.02 - 0.035 % |
Metal
- DIN 1652-3: Grade 22CrMoS3-5 Cold-Drawn Steel – High Strength & Durability for Automotive & Mechanical Applications
- DIN 1652-3 Grade 20Cr4 Cold-Drawn Steel: High-Performance Wear-Resistant Material
- DIN 1652-3 Grade 20CrS4 Cold‑Drawn Steel – High Wear Resistance & Superior Machinability
- DIN 1652-3 Grade 20MnCrS5 Cold-Drawn Steel – Superior Strength & Machinability
- DIN 1652-3 Grade 20MoCr4 Cold-Drawn Steel – High Strength & Durability
- 15CrNi6 Grade 15/20 Cold-Drawn Steel – Superior Strength & Toughness for Automotive & Mechanical Parts
- DIN 1652-3 Grade 16MnCr5 Cold-Drawn Steel – High Strength & Toughness for Automotive & Mechanical Applications
- DIN 1652-3 Grade 16MnCrS5 Cold Drawn Steel – High Strength & Precision
- DIN 1652-3 Grade 17Cr3 Cold-Drawn Steel – High Wear Resistance for Automotive & Mechanical Parts
- DIN 1652-3 Grade 17CrNiMo6 Cold‑Drawn Steel – High Strength & Durability