DIN 1652-3 Grade 17CrNiMo6 Cold‑Drawn Steel – High Strength & Durability

The steel 17 CrNiMo 6 is used for high loaded parts in the vehicle and mechanical engineering with high demands on toughness and core strength (e.g. gear parts, drive pinions). The lowest application amounts to -60 °C.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

7.8 g/cm³

Mechanical

PropertyTemperatureValueComment

Elastic modulus

-100.0 °C

217 GPa

20.0 °C

212 GPa

100.0 °C

207 GPa

200.0 °C

199 GPa

300.0 °C

192 GPa

400.0 °C

184 GPa

500.0 °C

175 GPa

600.0 °C

164 GPa

Poisson's ratio

23.0 °C

0.29 [-]

Typical for Nickel Chromium Molybdenum Steel

Tensile strength

20.0 °C

820 - 900 MPa

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

-100.0 °C

1.05E-5 1/K

20.0 °C

1.15E-5 1/K

100.0 °C

1.21E-5 1/K

200.0 °C

1.27E-5 1/K

300.0 °C

1.32E-5 1/K

400.0 °C

1.36E-5 1/K

500.0 °C

1.4E-5 1/K

600.0 °C

1.44E-5 1/K

Max service temperature, long

-60 - 0 °C

Melting point

1382 - 1529 °C

Typical for Nickel Chromium Molybdenum Steel

Specific heat capacity

-100.0 °C

423 J/(kg·K)

20.0 °C

461 J/(kg·K)

100.0 °C

479 J/(kg·K)

200.0 °C

499 J/(kg·K)

300.0 °C

517 J/(kg·K)

400.0 °C

536 J/(kg·K)

500.0 °C

558 J/(kg·K)

600.0 °C

587 J/(kg·K)

Thermal conductivity

20.0 °C

33.7 W/(m·K)

100.0 °C

36.2 W/(m·K)

200.0 °C

37.8 W/(m·K)

300.0 °C

37.2 W/(m·K)

400.0 °C

35.7 W/(m·K)

500.0 °C

34 W/(m·K)

600.0 °C

32 W/(m·K)

Thermal diffusivity

20.0 °C

9.4 mm²/s

100.0 °C

9.4 mm²/s

200.0 °C

9.2 mm²/s

300.0 °C

8.5 mm²/s

400.0 °C

7.6 mm²/s

500.0 °C

6.6 mm²/s

600.0 °C

5.4 mm²/s

Electrical

PropertyTemperatureValue

Electrical resistivity

20.0 °C

3.09E-7 Ω·m

100.0 °C

3.54E-7 Ω·m

200.0 °C

4.18E-7 Ω·m

300.0 °C

5.05E-7 Ω·m

400.0 °C

6.09E-7 Ω·m

500.0 °C

7.27E-7 Ω·m

600.0 °C

8.67E-7 Ω·m

Chemical properties

PropertyValue

Carbon

0.15 - 0.2 %

Chromium

1.5 - 1.8 %

Manganese

0.4 - 0.6 %

Molybdenum

0.25 - 0.35 %

Nickel

1.4 - 1.7 %

Phosphorus

0.04 %

Silicon

0.4 %

Sulfur

0.035 %


Metal

  • Metal
  • Resin
  • fiber
  • Composite material
  • Nanomaterials
  • Polymer Materials
  • Biologics
  • Dye
  • Spices
    1. DIN 1652-3 Grade 20MoCrS4 Cold-Drawn Steel: Ideal for Wear-Resistant Mechanical Components
    2. DIN 1652-3: Grade 22CrMoS3-5 Cold-Drawn Steel – High Strength & Durability for Automotive & Mechanical Applications
    3. DIN 1652-3 Grade 20Cr4 Cold-Drawn Steel: High-Performance Wear-Resistant Material
    4. DIN 1652-3 Grade 20CrS4 Cold‑Drawn Steel – High Wear Resistance & Superior Machinability
    5. DIN 1652-3 Grade 20MnCrS5 Cold-Drawn Steel – Superior Strength & Machinability
    6. DIN 1652-3 Grade 20MoCr4 Cold-Drawn Steel – High Strength & Durability
    7. 15CrNi6 Grade 15/20 Cold-Drawn Steel – Superior Strength & Toughness for Automotive & Mechanical Parts
    8. DIN 1652-3 Grade 16MnCr5 Cold-Drawn Steel – High Strength & Toughness for Automotive & Mechanical Applications
    9. DIN 1652-3 Grade 16MnCrS5 Cold Drawn Steel – High Strength & Precision
    10. DIN 1652-3 Grade 17Cr3 Cold-Drawn Steel – High Wear Resistance for Automotive & Mechanical Parts