DIN 17470 CrAl25-5 Soft Annealed: Premium Ferritic Conductor for High‑Temperature Applications
Ferritic heating conductor material for extrem alternating temperature loading at highest temperatures (about 1300 °C). Application: heating conductor material, exhaust-gas catalysts
Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 20.0 °C | 7.1 g/cm³ |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elastic modulus | 23.0 °C | 220 GPa | Typical for Ferritic Stainless Steel |
Elongation A100 | 20.0 °C | 6 - 12 % | |
Poisson's ratio | 23.0 °C | 0.3 [-] | Typical for Ferritic Stainless Steel |
Shear modulus | 23.0 °C | 77 GPa | Typical for Ferritic Stainless Steel |
Tensile strength | 20.0 °C | 600 MPa |
Thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 200.0 °C | 1.1E-5 1/K | |
400.0 °C | 1.2E-5 1/K | ||
600.0 °C | 1.3E-5 1/K | ||
800.0 °C | 1.4E-5 1/K | ||
1000.0 °C | 1.5E-5 1/K | ||
Max service temperature, long | 0 - 1300 °C | ||
Melting point | 1425 - 1530 °C | Typical for Ferritic Stainless Steel | |
Specific heat capacity | 20.0 °C | 460 J/(kg·K) | |
1000.0 °C | 630 J/(kg·K) | ||
Thermal conductivity | 20.0 °C | 13 W/(m·K) | |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical resistivity | 20.0 °C | 1.44E-6 Ω·m |
100.0 °C | 1.44E-6 Ω·m | |
200.0 °C | 1.44E-6 Ω·m | |
300.0 °C | 1.44E-6 Ω·m | |
400.0 °C | 1.45E-6 Ω·m | |
500.0 °C | 1.45E-6 Ω·m | |
600.0 °C | 1.46E-6 Ω·m | |
700.0 °C | 1.47E-6 Ω·m | |
800.0 °C | 1.48E-6 Ω·m | |
900.0 °C | 1.49E-6 Ω·m | |
1000.0 °C | 1.49E-6 Ω·m | |
1100.0 °C | 1.49E-6 Ω·m | |
1200.0 °C | 1.49E-6 Ω·m | |
Chemical properties
| Property | Value |
|---|---|
Aluminium | 4.5 - 6 % |
Carbon | 0.1 % |
Chromium | 22 - 25 % |
Manganese | 0.6 % |
Phosphorus | 0.05 % |
Silicon | 1 % |
Sulfur | 0.03 % |
Metal
- DIN 17442 X38CrMoV15 Soft-Annealed Stainless Steel – Superior Corrosion Resistance
- DIN 17210 Grade 21NiCrMo2 Soft Annealed Steel – Superior Wear Resistance & Fatigue Strength
- DIN 17210 Grade 20CrS4 Soft Annealed Steel: High Wear Resistance & Machinability
- DIN 17210 Grade 21NiCrMoS2 Soft Annealed Steel (+A) – High Performance for Wear-Resistant Applications
- DIN 17210 Grade 20Cr4 Soft‑Annealed Steel – High Wear Resistance for Automotive & Mechanical Applications
- DIN 17210 Grade 20MoCrS4 Soft Annealed Steel – Superior Wear Resistance & Fatigue Strength
- DIN 17210 Grade 16MnCr5 Soft Annealed Steel (+A) – High Strength & Toughness for Automotive & Mechanical Use
- DIN 17210 16MnCrS5 Soft Annealed Steel (+A): Superior Strength & Machinability
- DIN 2391-2 St 30 Al Seamless Steel Tube – Soft Annealed, Grade A
- DIN 2391-2 St 30 Si Soft‑Annealed Tube – Grade A for Precision Construction